- 缺口沖擊強度: 0.48
- 彎曲模量 [MPa]: 5.17
- 熱變形溫度 [℃]: 207.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.44 g/cc | 1.44 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm | 0.0050 - 0.0070 in/in @Thickness 0.126 in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm | 0.0070 - 0.0090 in/in @Thickness 0.126 in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 92.0 MPa | 13300 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | brk, 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.17 GPa | 750 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.50 J/cm | 4.68 ft-lb/in | ASTM D4812 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 207 °C @Thickness 3.20 mm | 405 °F @Thickness 0.126 in | unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C @Thickness 3.20 mm | 356 °F @Thickness 0.126 in | unannealed; ASTM D648 |