- 熔體流動(dòng)速率 [g/10min]: 13.0
- 密度 [g/cm3]: 1.57
- 吸水率 [%]: 0.5
- 缺口沖擊強(qiáng)度: 0.8
- 拉伸強(qiáng)度 [MPa]: 100.0
- 彎曲模量 [MPa]: 6.70
- 熱變形溫度 [℃]: 250.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in3 | DIN 53479 |
| Water Absorption | 0.50 % | 0.50 % | DIN 53495 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23° C, 50% RH; DIN 53714 |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | |
| Melt Flow | 13 g/10 min @Load 2.16 kg, Temperature 280 °C | 13 g/10 min @Load 4.76 lb, Temperature 536 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 100 MPa | 14500 psi | ASTM-D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM-D638 |
| Flexural Strength | 150 MPa | 21800 psi | ASTM D790 |
| Flexural Modulus | 6.70 GPa | 972 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.800 J/cm @Temperature 23.0 °C | 1.50 ft-lb/in @Temperature 73.4 °F | ASTM-D256 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | DIN 53482 |
| Dielectric Constant | 3.6 @Frequency 1e+6 Hz | 3.6 @Frequency 1e+6 Hz | VDE 0303/4 |
| Dielectric Strength | 29.0 kV/mm | 737 kV/in | VDE 0303/4 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | DIN 53461 |
| Deflection Temperature at 1.8 MPa (264 psi) | 226 °C | 439 °F | DIN 53461 |
| Flammability, UL94 | V-2 @Thickness 3.00 mm | V-2 @Thickness 0.118 in | |
| Glow Wire Test | 960 °C | 1760 °F | |
- 關(guān)鍵詞:
- PET
- 供應(yīng)
- Polyram PE322G22 PET
- 22% Glass Fiber