- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.22
- 缺口沖擊強度: 8.01
- 拉伸強度 [MPa]: 54.5
- 彎曲模量 [MPa]: 2.17
- 熱變形溫度 [℃]: 121.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0050 - 0.0080 cm/cm | 0.0050 - 0.0080 in/in | ASTM D955 |
| Melt Flow | 5.0 - 15 g/10 min | 5.0 - 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 55.2 MPa | 8000 psi | ASTM D638 |
| Tensile Strength, Yield | 54.5 MPa | 7900 psi | ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.17 GPa | 315 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Gardner Impact | >= 36.2 J | >= 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 121 °C | 250 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/16 in |
| HB | HB | 1/8 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |
| Middle Barrel Temperature | 254 - 277 °C | 490 - 530 °F | |
| Front Barrel Temperature | 260 - 282 °C | 500 - 540 °F | |
| Melt Temperature | 246 - 274 °C | 475 - 525 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |