- 密度 [g/cm3]: 1.65
- 彎曲強度 [MPa]: 126.0
- 彎曲模量 [MPa]: 9.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.65 g/cc | 0.0596 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 126 MPa | 18300 psi | ISO 527-1, 2 |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527-1, 2 |
| Flexural Strength | 215 MPa | 31200 psi | ISO 178 |
| Flexural Modulus | 9.20 GPa | 1330 ksi | ISO 178 |
| Charpy Impact, Notched | 0.730 J/cm2 | 3.47 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 7.00e+16 ohm-cm | 7.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 7.00e+16 ohm | 7.00e+16 ohm | IEC 60093 |
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 228 °C | 442 °F | ISO 75-1, 2 |
| Flammability, UL94 | V-0 | V-0 | |