- 熔體流動速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.24
- 缺口沖擊強度: 8.01
- 拉伸強度 [MPa]: 44.1
- 彎曲模量 [MPa]: 1.79
- 熱變形溫度 [℃]: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.013 - 0.018 cm/cm | 0.013 - 0.018 in/in | ASTM D955 |
| Melt Flow | 5.0 - 15 g/10 min | 5.0 - 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 46.2 MPa | 6700 psi | ASTM D638 |
| Tensile Strength, Yield | 44.1 MPa | 6400 psi | ASTM D638 |
| Flexural Strength | 66.2 MPa | 9600 psi | ASTM D790 |
| Flexural Modulus | 1.79 GPa | 260 ksi | ASTM D790 |
| Izod Impact, Notched | 8.01 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Gardner Impact | >= 36.2 J | >= 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 76.7 °C | 170 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/8 in |
| HB | HB | 1/16 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 227 - 243 °C | 440 - 470 °F | |
| Middle Barrel Temperature | 232 - 249 °C | 450 - 480 °F | |
| Front Barrel Temperature | 238 - 260 °C | 460 - 500 °F | |
| Melt Temperature | 238 - 260 °C | 460 - 500 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |