- 密度 [g/cm3]: 1.59
- 彎曲強度 [MPa]: 134.0
- 彎曲模量 [MPa]: 9.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 134 MPa | 19400 psi | ISO 527-1, 2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1, 2 |
| Flexural Strength | 203 MPa | 29400 psi | ISO 178 |
| Flexural Modulus | 9.30 GPa | 1350 ksi | ISO 178 |
| Charpy Impact, Notched | 0.860 J/cm2 | 4.09 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 2.00e+15 ohm-cm | 2.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 3.00e+16 ohm | 3.00e+16 ohm | IEC 60093 |
| Dielectric Strength | 23.0 kV/mm | 584 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 250 V | 250 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 234 °C | 453 °F | ISO 75-1, 2 |
| Flammability, UL94 | HB | HB | |