- 密度 [g/cm3]: 1.47
- 彎曲強度 [MPa]: 103.0
- 彎曲模量 [MPa]: 6.30
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.47 g/cc | 0.0531 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 103 MPa | 14900 psi | ISO 527-1, 2 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-1, 2 |
| Flexural Strength | 168 MPa | 24400 psi | ISO 178 |
| Flexural Modulus | 6.30 GPa | 914 ksi | ISO 178 |
| Charpy Impact, Notched | 0.450 J/cm2 | 2.14 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+17 ohm-cm | 1.00e+17 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 225 V | 225 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 222 °C | 432 °F | ISO 75-1, 2 |
| Flammability, UL94 | HB | HB | |