- 密度 [g/cm3]: 1.6
- 彎曲強度 [MPa]: 147.0
- 彎曲模量 [MPa]: 10.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.60 g/cc | 0.0578 lb/in3 | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 147 MPa | 21300 psi | ISO 527-1, 2 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527-1, 2 |
| Flexural Strength | 241 MPa | 35000 psi | ISO 178 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | ISO 178 |
| Charpy Impact, Notched | 0.830 J/cm2 | 3.95 ft-lb/in2 | ISO 179/1eA |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 6.00e+16 ohm-cm | 6.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+17 ohm | 1.00e+17 ohm | IEC 60093 |
| Dielectric Strength | 21.0 kV/mm | 533 kV/in | IEC 60243-1 |
| Comparative Tracking Index | 200 V | 200 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 238 °C | 460 °F | ISO 75-1, 2 |
| Flammability, UL94 | HB | HB | |