- 熔體流動速率 [g/10min]: 1.0
- 密度 [g/cm3]: 1.35
- 缺口沖擊強度: 1.07
- 拉伸強度 [MPa]: 72.4
- 彎曲模量 [MPa]: 4.69
- 熱變形溫度 [℃]: 116.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 1.0 - 6.0 g/10 min | 1.0 - 6.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 72.4 MPa | 10500 psi | ASTM D638 |
| Tensile Strength, Yield | 72.4 MPa | 10500 psi | ASTM D638 |
| Flexural Strength | 121 MPa | 17500 psi | ASTM D790 |
| Flexural Modulus | 4.69 GPa | 680 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm | 2.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 116 °C | 240 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 263 - 285 °C | 505 - 545 °F | |
| Middle Barrel Temperature | 268 - 291 °C | 515 - 555 °F | |
| Front Barrel Temperature | 274 - 296 °C | 525 - 565 °F | |
| Melt Temperature | 260 - 288 °C | 500 - 550 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |