- 熔體流動(dòng)速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.22
- 缺口沖擊強(qiáng)度: 8.54
- 拉伸強(qiáng)度 [MPa]: 50.3
- 彎曲模量 [MPa]: 2.07
- 熱變形溫度 [℃]: 98.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage | 0.0060 - 0.0090 cm/cm | 0.0060 - 0.0090 in/in | ASTM D955 |
| Melt Flow | 5.0 - 15 g/10 min | 5.0 - 15 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 51.7 MPa | 7500 psi | ASTM D638 |
| Tensile Strength, Yield | 50.3 MPa | 7300 psi | ASTM D638 |
| Flexural Strength | 74.5 MPa | 10800 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| 4.27 J/cm @Temperature -40.0 °C | 8.00 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Gardner Impact | >= 36.2 J | >= 26.7 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 98.9 °C | 210 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.3 °C | 200 °F | ASTM D648 |
| Flammability, UL94 | HB | HB | 1/16 in |
| HB | HB | 1/8 in | |
| Processing Properties | Metric | English | Comments |
| Rear Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |
| Middle Barrel Temperature | 254 - 277 °C | 490 - 530 °F | |
| Front Barrel Temperature | 260 - 282 °C | 500 - 540 °F | |
| Melt Temperature | 246 - 274 °C | 475 - 525 °F | |
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |
| Drying Temperature | 104 - 110 °C | 220 - 230 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |