- 密度 [g/cm3]: 1.37
- 缺口沖擊強度: 10.0
- 拉伸強度 [MPa]: 40.0
- 彎曲模量 [MPa]: 2.10
- 熱變形溫度 [℃]: 125.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in3 | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.020 cm/cm @Thickness 2.00 mm | 0.020 in/in @Thickness 0.0787 in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.016 cm/cm @Thickness 2.00 mm | 0.016 in/in @Thickness 0.0787 in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 40.0 MPa @Temperature 23.0 °C | 5800 psi @Temperature 73.4 °F | ISO 527 | ||
| Elongation at Break | 45 % @Temperature 23.0 °C | 45 % @Temperature 73.4 °F | nominal; ISO 527 | ||
| Elongation at Yield | 9.0 % @Temperature 23.0 °C | 9.0 % @Temperature 73.4 °F | ISO 527 | ||
| Tensile Modulus | 2.20 GPa @Temperature 23.0 °C | 319 ksi @Temperature 73.4 °F | ISO 527 | ||
| Flexural Modulus | 2.10 GPa @Temperature 23.0 °C | 305 ksi @Temperature 73.4 °F | ISO 178 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 @Temperature -40.0 °C | 4.76 ft-lb/in2 @Temperature -40.0 °F | ISO 180/1A | ||
| 10.0 kJ/m2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1A | |||
| 70.0 kJ/m2 @Temperature 23.0 °C | 33.3 ft-lb/in2 @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 220 kJ/m2 @Temperature -40.0 °C | 105 ft-lb/in2 @Temperature -40.0 °F | ISO 180/1U | ||
| 220 kJ/m2 @Temperature -30.0 °C | 105 ft-lb/in2 @Temperature -22.0 °F | ISO 180/1U | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 180/1U | |||
| Charpy Impact Unnotched | 35.0 J/cm2 @Temperature -40.0 °C | 167 ft-lb/in2 @Temperature -40.0 °F | ISO 179/1eU | ||
| 35.0 J/cm2 @Temperature -30.0 °C | 167 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.00 J/cm2 @Temperature -40.0 °C | 4.76 ft-lb/in2 @Temperature -40.0 °F | ISO 179/1eA | ||
| 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| 6.50 J/cm2 @Temperature 23.0 °C | 30.9 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | >= 600 V @Temperature 23.0 °C | >= 600 V @Temperature 73.4 °F | UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | ||
| 130 °C @Thickness 0.850 mm | 266 °F @Thickness 0.0335 in | UL 746B | |||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| UL RTI, Mechanical with Impact | 130 °C @Thickness 0.850 mm | 266 °F @Thickness 0.0335 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| UL RTI, Mechanical without Impact | 130 °C @Thickness 0.850 mm | 266 °F @Thickness 0.0335 in | UL 746B | ||
| 130 °C @Thickness 1.50 mm | 266 °F @Thickness 0.0591 in | UL 746B | |||
| 130 °C @Thickness 3.00 mm | 266 °F @Thickness 0.118 in | UL 746B | |||
| Flammability, UL94 | V-0 @Thickness 0.850 mm | V-0 @Thickness 0.0335 in | IEC 60695-11-10 | ||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | IEC 60695-11-10 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | IEC 60695-11-10 | |||
| V-0 @Thickness 0.850 mm | V-0 @Thickness 0.0335 in | UL94 | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | UL94 | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 | ||
| 250 °C | 482 °F | Optimum | |||
| 240 - 260 °C | 464 - 500 °F | ||||
| Mold Temperature | 80.0 °C | 176 °F | optimum | ||
| 30.0 - 130 °C | 86.0 - 266 °F | ||||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.040 % | <= 0.040 % | |||
| Descriptive Properties | |||||
| Additive | Impact Modifier | ||||
| Lubricant | |||||
| UV Stabilizer | |||||
| Appearance | Natural Color | ||||
| Drying Recommended | Yes | ||||
| Features | Chemical Resistance, Good | ||||
| Dimensional Stability, Good | |||||
| Flame Retardant | |||||
| Impact Resistance, High | |||||
| Moisture Absorption, Low | |||||
| Processability, Good | |||||
| UV Resistance, Good | |||||
| Forms | Pellets | ||||
| Generic | PBT | ||||
| Material Status | Current | ||||
| Part Marking Code | >PBT-HIFR(17)< | ISO 11469 | |||
| Processing Method | Injection Molding | ||||
| Product Category | Extrusion Resins | ||||
| Flame Retardant Resins | |||||
| Toughened Resins | |||||
| UV Resistant/Weatherable Resins | |||||
| Resin Identification | PBT-HIFR(17) | ISO 1043 | |||
| RoHS Compliance | Contact Manufacturer | ||||
| Uses | Connectors | ||||
| Electrical/Electronic Applications | |||||