- 熔體流動(dòng)速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.18
- 缺口沖擊強(qiáng)度: 65.0
- 拉伸強(qiáng)度 [MPa]: 36.0
- 熱變形溫度 [℃]: 85.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.18 g/cc | 0.0426 lb/in3 | |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 250 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 482 °F | cm3/10 min |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break (50 mm/min) |
| Elongation at Yield | 3.9 % | 3.9 % | 50 mm/min |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min |
| Izod Impact, Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Izod Impact, Notched (ISO) | 65.0 kJ/m2 @Temperature -30.0 °C | 30.9 ft-lb/in2 @Temperature -22.0 °F | |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 500 V | 500 V | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 113 °C | 235 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |