- 熔體流動速率 [g/10min]: 2.1
- 密度 [g/cm3]: 1.2
- 缺口沖擊強度: 44.0
- 拉伸強度 [MPa]: 55.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | |
| Melt Flow | 2.1 g/10 min @Load 2.16 kg, Temperature 250 °C | 2.1 g/10 min @Load 4.76 lb, Temperature 482 °F | cm3/10 min |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal strain at break (50 mm/min) |
| Elongation at Yield | 5.5 % | 5.5 % | 50 mm/min |
| Tensile Modulus | 2.15 GPa | 312 ksi | 1 mm/min |
| Izod Impact, Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Izod Impact, Notched (ISO) | 44.0 kJ/m2 @Temperature -30.0 °C | 20.9 ft-lb/in2 @Temperature -22.0 °F | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 125 °C | 257 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |