| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ASTM D792 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 124 MPa | 18000 psi | ASTM D638 | ||
| Elongation at Break | 2.0 % | 2.0 % | ASTM D638 | ||
| Flexural Strength | 186 MPa | 27000 psi | ASTM D790 | ||
| Flexural Modulus | 6.89 GPa | 1000 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | 73°F; ASTM D256 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 232 - 243 °C | 450 - 470 °F | |||
| Middle Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |||
| Front Barrel Temperature | 243 - 254 °C | 470 - 490 °F | |||
| Nozzle Temperature | 243 - 254 °C | 470 - 490 °F | |||
| Melt Temperature | 249 - 260 °C | 480 - 500 °F | |||
| Mold Temperature | 82.2 - 121 °C | 180 - 250 °F | |||
| Drying Temperature | 121 °C | 250 °F | |||
| Dry Time | <= 12 hour | <= 12 hour | |||
| Moisture Content | <= 0.020 % | <= 0.020 % | |||
| Injection Pressure | 6.89 - 11.7 MPa | 1000 - 1700 psi | |||
| Back Pressure | 0.138 - 0.414 MPa | 20.0 - 60.0 psi | |||
| Shot Size | 40 - 80 % | 40 - 80 % | |||
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm | |||
| Descriptive Properties | |||||
| Injection Rate | Moderate-Fast | ||||