密度 [g/cm3]: 1.22
吸水率 [%]: 0.12
缺口沖擊強度: 1.17
拉伸強度 [MPa]: 38.0
彎曲模量 [MPa]: 0.137
硬度: 98.0
熱變形溫度 [℃]: 100.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.23 g/cc	1.23 g/cc	ASTM D792
Density	1.22 g/cc	0.0441 lb/in3	ISO 1183
Water Absorption	0.12 % @Temperature 23.0 °C	0.12 % @Temperature 73.4 °F	Equilibrium 50%RH; ISO 62, Similar to
	0.31 % @Temperature 23.0 °C	0.31 % @Temperature 73.4 °F	Saturation, immersed; ISO 62, Similar to
Linear Mold Shrinkage	0.022 cm/cm	0.022 in/in	Flow
	0.030 cm/cm	0.030 in/in	Transverse
Linear Mold Shrinkage, Flow	0.025 cm/cm	0.025 in/in	Parallel; Annealed; ISO 294-4
	0.019 cm/cm @Thickness 2.00 mm	0.019 in/in @Thickness 0.0787 in	Parallel; ISO 294-4
Linear Mold Shrinkage, Transverse	0.0225 cm/cm	0.0225 in/in	Normal; Annealed; ISO 294-4
	0.018 cm/cm @Thickness 2.00 mm	0.018 in/in @Thickness 0.0787 in	Normal; ISO 294-4
Melt Index of Compound	5.0 g/10 min	5.0 g/10 min	cm3/10 min; ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	98	98	ASTM D785
	104	104	ISO 2039/2
Tensile Strength at Break	21.0 MPa @Temperature 100 °C	3050 psi @Temperature 212 °F	ISO 527
	71.0 MPa @Temperature -40.0 °C	10300 psi @Temperature -40.0 °F	ISO 527
Tensile Strength	21.0 MPa @Temperature 149 °C	3050 psi @Temperature 300 °F	ASTM D638
	28.0 MPa @Temperature 90.0 °C	4060 psi @Temperature 194 °F	ASTM D638
	37.0 MPa @Temperature 23.0 °C	5370 psi @Temperature 73.4 °F	ASTM D638
	68.0 MPa @Temperature -40.0 °C	9860 psi @Temperature -40.0 °F	ASTM D638
Tensile Stress	0.310 MPa @Strain 0.200 %, Temperature 150 °C	45.0 psi @Strain 0.200 %, Temperature 302 °F	ISO 11403-1/-2
	0.320 MPa @Strain 0.100 %, Temperature 150 °C	46.4 psi @Strain 0.100 %, Temperature 302 °F	ISO 11403-1/-2
	0.500 MPa @Strain 0.100 %, Temperature 80.0 °C	72.5 psi @Strain 0.100 %, Temperature 176 °F	ISO 11403-1/-2
	0.550 MPa @Strain 0.200 %, Temperature 100 °C	79.8 psi @Strain 0.200 %, Temperature 212 °F	ISO 11403-1/-2
	0.590 MPa @Strain 0.100 %, Temperature 120 °C	85.6 psi @Strain 0.100 %, Temperature 248 °F	ISO 11403-1/-2
	0.600 MPa @Strain 0.300 %, Temperature 150 °C	87.0 psi @Strain 0.300 %, Temperature 302 °F	ISO 11403-1/-2
	0.630 MPa @Strain 0.200 %, Temperature 80.0 °C	91.4 psi @Strain 0.200 %, Temperature 176 °F	ISO 11403-1/-2
	0.680 MPa @Strain 0.100 %, Temperature 60.0 °C	98.6 psi @Strain 0.100 %, Temperature 140 °F	ISO 11403-1/-2
	0.730 MPa @Strain 0.200 %, Temperature 120 °C	106 psi @Strain 0.200 %, Temperature 248 °F	ISO 11403-1/-2
	0.760 MPa @Strain 0.400 %, Temperature 150 °C	110 psi @Strain 0.400 %, Temperature 302 °F	ISO 11403-1/-2
	0.860 MPa @Strain 0.300 %, Temperature 100 °C	125 psi @Strain 0.300 %, Temperature 212 °F	ISO 11403-1/-2
	0.870 MPa @Strain 0.300 %, Temperature 120 °C	126 psi @Strain 0.300 %, Temperature 248 °F	ISO 11403-1/-2
	0.870 MPa @Strain 0.300 %, Temperature 80.0 °C	126 psi @Strain 0.300 %, Temperature 176 °F	ISO 11403-1/-2
	0.890 MPa @Strain 0.500 %, Temperature 150 °C	129 psi @Strain 0.500 %, Temperature 302 °F	ISO 11403-1/-2
	1.00 MPa @Strain 0.400 %, Temperature 120 °C	145 psi @Strain 0.400 %, Temperature 248 °F	ISO 11403-1/-2
	1.04 MPa @Strain 0.600 %, Temperature 150 °C	151 psi @Strain 0.600 %, Temperature 302 °F	ISO 11403-1/-2
	1.04 MPa @Strain 0.400 %, Temperature 100 °C	151 psi @Strain 0.400 %, Temperature 212 °F	ISO 11403-1/-2
	1.10 MPa @Strain 0.200 %, Temperature 60.0 °C	160 psi @Strain 0.200 %, Temperature 140 °F	ISO 11403-1/-2
	1.15 MPa @Strain 0.400 %, Temperature 80.0 °C	167 psi @Strain 0.400 %, Temperature 176 °F	ISO 11403-1/-2
	1.18 MPa @Strain 0.700 %, Temperature 150 °C	171 psi @Strain 0.700 %, Temperature 302 °F	ISO 11403-1/-2
	1.18 MPa @Strain 0.500 %, Temperature 120 °C	171 psi @Strain 0.500 %, Temperature 248 °F	ISO 11403-1/-2
	1.25 MPa @Strain 0.500 %, Temperature 100 °C	181 psi @Strain 0.500 %, Temperature 212 °F	ISO 11403-1/-2
	1.26 MPa @Strain 0.800 %, Temperature 150 °C	183 psi @Strain 0.800 %, Temperature 302 °F	ISO 11403-1/-2
	1.36 MPa @Strain 0.600 %, Temperature 120 °C	197 psi @Strain 0.600 %, Temperature 248 °F	ISO 11403-1/-2
	1.38 MPa @Strain 0.500 %, Temperature 80.0 °C	200 psi @Strain 0.500 %, Temperature 176 °F	ISO 11403-1/-2
	1.39 MPa @Strain 0.900 %, Temperature 150 °C	202 psi @Strain 0.900 %, Temperature 302 °F	ISO 11403-1/-2
	1.42 MPa @Strain 0.300 %, Temperature 60.0 °C	206 psi @Strain 0.300 %, Temperature 140 °F	ISO 11403-1/-2
	1.49 MPa @Strain 0.700 %, Temperature 120 °C	216 psi @Strain 0.700 %, Temperature 248 °F	ISO 11403-1/-2
	1.53 MPa @Strain 1.00 %, Temperature 150 °C	222 psi @Strain 1.00 %, Temperature 302 °F	ISO 11403-1/-2
	1.53 MPa @Strain 0.600 %, Temperature 100 °C	222 psi @Strain 0.600 %, Temperature 212 °F	ISO 11403-1/-2
	1.61 MPa @Strain 1.10 %, Temperature 150 °C	234 psi @Strain 1.10 %, Temperature 302 °F	ISO 11403-1/-2
	1.61 MPa @Strain 0.600 %, Temperature 80.0 °C	234 psi @Strain 0.600 %, Temperature 176 °F	ISO 11403-1/-2
	1.66 MPa @Strain 0.800 %, Temperature 120 °C	241 psi @Strain 0.800 %, Temperature 248 °F	ISO 11403-1/-2
	1.72 MPa @Strain 0.700 %, Temperature 100 °C	249 psi @Strain 0.700 %, Temperature 212 °F	ISO 11403-1/-2
	1.73 MPa @Strain 1.20 %, Temperature 150 °C	251 psi @Strain 1.20 %, Temperature 302 °F	ISO 11403-1/-2
	1.82 MPa @Strain 0.400 %, Temperature 60.0 °C	264 psi @Strain 0.400 %, Temperature 140 °F	ISO 11403-1/-2
	1.86 MPa @Strain 0.900 %, Temperature 120 °C	270 psi @Strain 0.900 %, Temperature 248 °F	ISO 11403-1/-2
	1.87 MPa @Strain 1.30 %, Temperature 150 °C	271 psi @Strain 1.30 %, Temperature 302 °F	ISO 11403-1/-2
	1.87 MPa @Strain 0.700 %, Temperature 80.0 °C	271 psi @Strain 0.700 %, Temperature 176 °F	ISO 11403-1/-2
	1.93 MPa @Strain 0.800 %, Temperature 100 °C	280 psi @Strain 0.800 %, Temperature 212 °F	ISO 11403-1/-2
	1.98 MPa @Strain 1.00 %, Temperature 120 °C	287 psi @Strain 1.00 %, Temperature 248 °F	ISO 11403-1/-2
	1.99 MPa @Strain 1.40 %, Temperature 150 °C	289 psi @Strain 1.40 %, Temperature 302 °F	ISO 11403-1/-2
	2.10 MPa @Strain 1.50 %, Temperature 150 °C	305 psi @Strain 1.50 %, Temperature 302 °F	ISO 11403-1/-2
	2.13 MPa @Strain 0.100 %, Temperature -40.0 °C	309 psi @Strain 0.100 %, Temperature -40.0 °F	ISO 11403-1/-2
	2.15 MPa @Strain 0.800 %, Temperature 80.0 °C	312 psi @Strain 0.800 %, Temperature 176 °F	ISO 11403-1/-2
	2.16 MPa @Strain 0.900 %, Temperature 100 °C	313 psi @Strain 0.900 %, Temperature 212 °F	ISO 11403-1/-2
	2.21 MPa @Strain 1.10 %, Temperature 120 °C	321 psi @Strain 1.10 %, Temperature 248 °F	ISO 11403-1/-2
	2.24 MPa @Strain 1.60 %, Temperature 150 °C	325 psi @Strain 1.60 %, Temperature 302 °F	ISO 11403-1/-2
	2.25 MPa @Strain 0.500 %, Temperature 60.0 °C	326 psi @Strain 0.500 %, Temperature 140 °F	ISO 11403-1/-2
	2.33 MPa @Strain 1.70 %, Temperature 150 °C	338 psi @Strain 1.70 %, Temperature 302 °F	ISO 11403-1/-2
	2.34 MPa @Strain 1.00 %, Temperature 100 °C	339 psi @Strain 1.00 %, Temperature 212 °F	ISO 11403-1/-2
	2.38 MPa @Strain 1.20 %, Temperature 120 °C	345 psi @Strain 1.20 %, Temperature 248 °F	ISO 11403-1/-2
	2.41 MPa @Strain 0.900 %, Temperature 80.0 °C	350 psi @Strain 0.900 %, Temperature 176 °F	ISO 11403-1/-2
	2.44 MPa @Strain 1.80 %, Temperature 150 °C	354 psi @Strain 1.80 %, Temperature 302 °F	ISO 11403-1/-2
	2.50 MPa @Strain 1.30 %, Temperature 120 °C	363 psi @Strain 1.30 %, Temperature 248 °F	ISO 11403-1/-2
	2.56 MPa @Strain 1.10 %, Temperature 100 °C	371 psi @Strain 1.10 %, Temperature 212 °F	ISO 11403-1/-2
	2.58 MPa @Strain 1.90 %, Temperature 150 °C	374 psi @Strain 1.90 %, Temperature 302 °F	ISO 11403-1/-2
	2.63 MPa @Strain 1.00 %, Temperature 80.0 °C	381 psi @Strain 1.00 %, Temperature 176 °F	ISO 11403-1/-2
	2.67 MPa @Strain 2.00 %, Temperature 150 °C	387 psi @Strain 2.00 %, Temperature 302 °F	ISO 11403-1/-2
	2.69 MPa @Strain 1.40 %, Temperature 120 °C	390 psi @Strain 1.40 %, Temperature 248 °F	ISO 11403-1/-2
	2.71 MPa @Strain 0.600 %, Temperature 60.0 °C	393 psi @Strain 0.600 %, Temperature 140 °F	ISO 11403-1/-2
	2.75 MPa @Strain 2.10 %, Temperature 150 °C	399 psi @Strain 2.10 %, Temperature 302 °F	ISO 11403-1/-2
	2.77 MPa @Strain 1.20 %, Temperature 100 °C	402 psi @Strain 1.20 %, Temperature 212 °F	ISO 11403-1/-2
	2.84 MPa @Strain 1.50 %, Temperature 120 °C	412 psi @Strain 1.50 %, Temperature 248 °F	ISO 11403-1/-2
	2.88 MPa @Strain 2.20 %, Temperature 150 °C	418 psi @Strain 2.20 %, Temperature 302 °F	ISO 11403-1/-2
	2.92 MPa @Strain 1.10 %, Temperature 80.0 °C	424 psi @Strain 1.10 %, Temperature 176 °F	ISO 11403-1/-2
	2.94 MPa @Strain 1.60 %, Temperature 120 °C	426 psi @Strain 1.60 %, Temperature 248 °F	ISO 11403-1/-2
	3.00 MPa @Strain 1.30 %, Temperature 100 °C	435 psi @Strain 1.30 %, Temperature 212 °F	ISO 11403-1/-2
	3.01 MPa @Strain 2.30 %, Temperature 150 °C	437 psi @Strain 2.30 %, Temperature 302 °F	ISO 11403-1/-2
	3.04 MPa @Strain 0.700 %, Temperature 60.0 °C	441 psi @Strain 0.700 %, Temperature 140 °F	ISO 11403-1/-2
	3.09 MPa @Strain 2.40 %, Temperature 150 °C	448 psi @Strain 2.40 %, Temperature 302 °F	ISO 11403-1/-2
	3.13 MPa @Strain 1.70 %, Temperature 120 °C	454 psi @Strain 1.70 %, Temperature 248 °F	ISO 11403-1/-2
	3.14 MPa @Strain 1.40 %, Temperature 100 °C	455 psi @Strain 1.40 %, Temperature 212 °F	ISO 11403-1/-2
	3.16 MPa @Strain 1.20 %, Temperature 80.0 °C	458 psi @Strain 1.20 %, Temperature 176 °F	ISO 11403-1/-2
	3.19 MPa @Strain 0.200 %, Temperature 23.0 °C	463 psi @Strain 0.200 %, Temperature 73.4 °F	ISO 11403-1/-2
	3.22 MPa @Strain 2.50 %, Temperature 150 °C	467 psi @Strain 2.50 %, Temperature 302 °F	ISO 11403-1/-2
	3.30 MPa @Strain 2.60 %, Temperature 150 °C	479 psi @Strain 2.60 %, Temperature 302 °F	ISO 11403-1/-2
	3.31 MPa @Strain 1.80 %, Temperature 120 °C	480 psi @Strain 1.80 %, Temperature 248 °F	ISO 11403-1/-2
	3.34 MPa @Strain 1.30 %, Temperature 80.0 °C	484 psi @Strain 1.30 %, Temperature 176 °F	ISO 11403-1/-2
	3.34 MPa @Strain 0.800 %, Temperature 60.0 °C	484 psi @Strain 0.800 %, Temperature 140 °F	ISO 11403-1/-2
	3.40 MPa @Strain 1.50 %, Temperature 100 °C	493 psi @Strain 1.50 %, Temperature 212 °F	ISO 11403-1/-2
	3.40 MPa @Strain 2.70 %, Temperature 150 °C	493 psi @Strain 2.70 %, Temperature 302 °F	ISO 11403-1/-2
	3.44 MPa @Strain 1.90 %, Temperature 120 °C	499 psi @Strain 1.90 %, Temperature 248 °F	ISO 11403-1/-2
	3.51 MPa @Strain 2.80 %, Temperature 150 °C	509 psi @Strain 2.80 %, Temperature 302 °F	ISO 11403-1/-2
	3.59 MPa @Strain 1.60 %, Temperature 100 °C	521 psi @Strain 1.60 %, Temperature 212 °F	ISO 11403-1/-2
	3.60 MPa @Strain 2.90 %, Temperature 150 °C	522 psi @Strain 2.90 %, Temperature 302 °F	ISO 11403-1/-2
	3.63 MPa @Strain 2.00 %, Temperature 120 °C	526 psi @Strain 2.00 %, Temperature 248 °F	ISO 11403-1/-2
	3.66 MPa @Strain 1.40 %, Temperature 80.0 °C	531 psi @Strain 1.40 %, Temperature 176 °F	ISO 11403-1/-2
	3.71 MPa @Strain 3.00 %, Temperature 150 °C	538 psi @Strain 3.00 %, Temperature 302 °F	ISO 11403-1/-2
	3.74 MPa @Strain 1.70 %, Temperature 100 °C	542 psi @Strain 1.70 %, Temperature 212 °F	ISO 11403-1/-2
	3.74 MPa @Strain 0.200 %, Temperature 0.000 °C	542 psi @Strain 0.200 %, Temperature 32.0 °F	ISO 11403-1/-2
	3.75 MPa @Strain 2.10 %, Temperature 120 °C	544 psi @Strain 2.10 %, Temperature 248 °F	ISO 11403-1/-2
	3.79 MPa @Strain 0.900 %, Temperature 60.0 °C	550 psi @Strain 0.900 %, Temperature 140 °F	ISO 11403-1/-2
	3.81 MPa @Strain 3.10 %, Temperature 150 °C	553 psi @Strain 3.10 %, Temperature 302 °F	ISO 11403-1/-2
	3.85 MPa @Strain 1.50 %, Temperature 80.0 °C	558 psi @Strain 1.50 %, Temperature 176 °F	ISO 11403-1/-2
	3.87 MPa @Strain 2.20 %, Temperature 120 °C	561 psi @Strain 2.20 %, Temperature 248 °F	ISO 11403-1/-2
	3.89 MPa @Strain 3.20 %, Temperature 150 °C	564 psi @Strain 3.20 %, Temperature 302 °F	ISO 11403-1/-2
	3.96 MPa @Strain 3.30 %, Temperature 150 °C	574 psi @Strain 3.30 %, Temperature 302 °F	ISO 11403-1/-2
	3.99 MPa @Strain 1.80 %, Temperature 100 °C	579 psi @Strain 1.80 %, Temperature 212 °F	ISO 11403-1/-2
	4.05 MPa @Strain 1.60 %, Temperature 80.0 °C	587 psi @Strain 1.60 %, Temperature 176 °F	ISO 11403-1/-2
	4.06 MPa @Strain 3.40 %, Temperature 150 °C	589 psi @Strain 3.40 %, Temperature 302 °F	ISO 11403-1/-2
	4.08 MPa @Strain 0.200 %, Temperature -40.0 °C	592 psi @Strain 0.200 %, Temperature -40.0 °F	ISO 11403-1/-2
	4.09 MPa @Strain 2.30 %, Temperature 120 °C	593 psi @Strain 2.30 %, Temperature 248 °F	ISO 11403-1/-2
	4.12 MPa @Strain 1.90 %, Temperature 100 °C	598 psi @Strain 1.90 %, Temperature 212 °F	ISO 11403-1/-2
	4.14 MPa @Strain 3.50 %, Temperature 150 °C	600 psi @Strain 3.50 %, Temperature 302 °F	ISO 11403-1/-2
	4.16 MPa @Strain 1.00 %, Temperature 60.0 °C	603 psi @Strain 1.00 %, Temperature 140 °F	ISO 11403-1/-2
	4.18 MPa @Strain 2.40 %, Temperature 120 °C	606 psi @Strain 2.40 %, Temperature 248 °F	ISO 11403-1/-2
	4.22 MPa @Strain 3.60 %, Temperature 150 °C	612 psi @Strain 3.60 %, Temperature 302 °F	ISO 11403-1/-2
	4.28 MPa @Strain 2.00 %, Temperature 100 °C	621 psi @Strain 2.00 %, Temperature 212 °F	ISO 11403-1/-2
	4.33 MPa @Strain 2.50 %, Temperature 120 °C	628 psi @Strain 2.50 %, Temperature 248 °F	ISO 11403-1/-2
	4.34 MPa @Strain 3.70 %, Temperature 150 °C	629 psi @Strain 3.70 %, Temperature 302 °F	ISO 11403-1/-2
	4.35 MPa @Strain 1.70 %, Temperature 80.0 °C	631 psi @Strain 1.70 %, Temperature 176 °F	ISO 11403-1/-2
	4.45 MPa @Strain 3.80 %, Temperature 150 °C	645 psi @Strain 3.80 %, Temperature 302 °F	ISO 11403-1/-2
	4.50 MPa @Strain 2.60 %, Temperature 120 °C	653 psi @Strain 2.60 %, Temperature 248 °F	ISO 11403-1/-2
	4.50 MPa @Strain 2.10 %, Temperature 100 °C	653 psi @Strain 2.10 %, Temperature 212 °F	ISO 11403-1/-2
	4.50 MPa @Strain 1.10 %, Temperature 60.0 °C	653 psi @Strain 1.10 %, Temperature 140 °F	ISO 11403-1/-2
	4.51 MPa @Strain 3.90 %, Temperature 150 °C	654 psi @Strain 3.90 %, Temperature 302 °F	ISO 11403-1/-2
	4.52 MPa @Strain 1.80 %, Temperature 80.0 °C	656 psi @Strain 1.80 %, Temperature 176 °F	ISO 11403-1/-2
	4.58 MPa @Strain 2.70 %, Temperature 120 °C	664 psi @Strain 2.70 %, Temperature 248 °F	ISO 11403-1/-2
	4.59 MPa @Strain 4.00 %, Temperature 150 °C	666 psi @Strain 4.00 %, Temperature 302 °F	ISO 11403-1/-2
	4.64 MPa @Strain 2.20 %, Temperature 100 °C	673 psi @Strain 2.20 %, Temperature 212 °F	ISO 11403-1/-2
	4.67 MPa @Strain 4.10 %, Temperature 150 °C	677 psi @Strain 4.10 %, Temperature 302 °F	ISO 11403-1/-2
	4.69 MPa @Strain 0.300 %, Temperature 23.0 °C	680 psi @Strain 0.300 %, Temperature 73.4 °F	ISO 11403-1/-2
	4.73 MPa @Strain 4.20 %, Temperature 150 °C	686 psi @Strain 4.20 %, Temperature 302 °F	ISO 11403-1/-2
	4.74 MPa @Strain 1.90 %, Temperature 80.0 °C	687 psi @Strain 1.90 %, Temperature 176 °F	ISO 11403-1/-2
	4.76 MPa @Strain 1.20 %, Temperature 60.0 °C	690 psi @Strain 1.20 %, Temperature 140 °F	ISO 11403-1/-2
	4.79 MPa @Strain 2.80 %, Temperature 120 °C	695 psi @Strain 2.80 %, Temperature 248 °F	ISO 11403-1/-2
	4.80 MPa @Strain 4.30 %, Temperature 150 °C	696 psi @Strain 4.30 %, Temperature 302 °F	ISO 11403-1/-2
	4.83 MPa @Strain 2.30 %, Temperature 100 °C	701 psi @Strain 2.30 %, Temperature 212 °F	ISO 11403-1/-2
	4.89 MPa @Strain 4.40 %, Temperature 150 °C	709 psi @Strain 4.40 %, Temperature 302 °F	ISO 11403-1/-2
	4.90 MPa @Strain 2.90 %, Temperature 120 °C	711 psi @Strain 2.90 %, Temperature 248 °F	ISO 11403-1/-2
	4.95 MPa @Strain 4.50 %, Temperature 150 °C	718 psi @Strain 4.50 %, Temperature 302 °F	ISO 11403-1/-2
	4.98 MPa @Strain 2.00 %, Temperature 80.0 °C	722 psi @Strain 2.00 %, Temperature 176 °F	ISO 11403-1/-2
	5.00 MPa @Strain 3.00 %, Temperature 120 °C	725 psi @Strain 3.00 %, Temperature 248 °F	ISO 11403-1/-2
	5.02 MPa @Strain 2.40 %, Temperature 100 °C	728 psi @Strain 2.40 %, Temperature 212 °F	ISO 11403-1/-2
	5.03 MPa @Strain 4.60 %, Temperature 150 °C	730 psi @Strain 4.60 %, Temperature 302 °F	ISO 11403-1/-2
	5.11 MPa @Strain 4.70 %, Temperature 150 °C	741 psi @Strain 4.70 %, Temperature 302 °F	ISO 11403-1/-2
	5.13 MPa @Strain 1.30 %, Temperature 60.0 °C	744 psi @Strain 1.30 %, Temperature 140 °F	ISO 11403-1/-2
	5.14 MPa @Strain 2.10 %, Temperature 80.0 °C	745 psi @Strain 2.10 %, Temperature 176 °F	ISO 11403-1/-2
	5.16 MPa @Strain 3.10 %, Temperature 120 °C	748 psi @Strain 3.10 %, Temperature 248 °F	ISO 11403-1/-2
	5.16 MPa @Strain 4.80 %, Temperature 150 °C	748 psi @Strain 4.80 %, Temperature 302 °F	ISO 11403-1/-2
	5.17 MPa @Strain 2.50 %, Temperature 100 °C	750 psi @Strain 2.50 %, Temperature 212 °F	ISO 11403-1/-2
	5.22 MPa @Strain 4.90 %, Temperature 150 °C	757 psi @Strain 4.90 %, Temperature 302 °F	ISO 11403-1/-2
	5.27 MPa @Strain 3.20 %, Temperature 120 °C	764 psi @Strain 3.20 %, Temperature 248 °F	ISO 11403-1/-2
	5.29 MPa @Strain 5.00 %, Temperature 150 °C	767 psi @Strain 5.00 %, Temperature 302 °F	ISO 11403-1/-2
	5.34 MPa @Strain 2.60 %, Temperature 100 °C	775 psi @Strain 2.60 %, Temperature 212 °F	ISO 11403-1/-2
	5.34 MPa @Strain 0.300 %, Temperature 0.000 °C	775 psi @Strain 0.300 %, Temperature 32.0 °F	ISO 11403-1/-2
	5.35 MPa @Strain 2.20 %, Temperature 80.0 °C	776 psi @Strain 2.20 %, Temperature 176 °F	ISO 11403-1/-2
	5.41 MPa @Strain 3.30 %, Temperature 120 °C	785 psi @Strain 3.30 %, Temperature 248 °F	ISO 11403-1/-2
	5.46 MPa @Strain 1.40 %, Temperature 60.0 °C	792 psi @Strain 1.40 %, Temperature 140 °F	ISO 11403-1/-2
	5.50 MPa @Strain 2.70 %, Temperature 100 °C	798 psi @Strain 2.70 %, Temperature 212 °F	ISO 11403-1/-2
	5.56 MPa @Strain 2.30 %, Temperature 80.0 °C	806 psi @Strain 2.30 %, Temperature 176 °F	ISO 11403-1/-2
	5.56 MPa @Strain 3.40 %, Temperature 120 °C	806 psi @Strain 3.40 %, Temperature 248 °F	ISO 11403-1/-2
	5.64 MPa @Strain 3.50 %, Temperature 120 °C	818 psi @Strain 3.50 %, Temperature 248 °F	ISO 11403-1/-2
	5.66 MPa @Strain 2.80 %, Temperature 100 °C	821 psi @Strain 2.80 %, Temperature 212 °F	ISO 11403-1/-2
	5.74 MPa @Strain 3.60 %, Temperature 120 °C	833 psi @Strain 3.60 %, Temperature 248 °F	ISO 11403-1/-2
	5.76 MPa @Strain 6.00 %, Temperature 150 °C	835 psi @Strain 6.00 %, Temperature 302 °F	ISO 11403-1/-2
	5.78 MPa @Strain 2.90 %, Temperature 100 °C	838 psi @Strain 2.90 %, Temperature 212 °F	ISO 11403-1/-2
	5.79 MPa @Strain 1.50 %, Temperature 60.0 °C	840 psi @Strain 1.50 %, Temperature 140 °F	ISO 11403-1/-2
	5.81 MPa @Strain 2.40 %, Temperature 80.0 °C	843 psi @Strain 2.40 %, Temperature 176 °F	ISO 11403-1/-2
	5.89 MPa @Strain 3.70 %, Temperature 120 °C	854 psi @Strain 3.70 %, Temperature 248 °F	ISO 11403-1/-2
	5.95 MPa @Strain 3.00 %, Temperature 100 °C	863 psi @Strain 3.00 %, Temperature 212 °F	ISO 11403-1/-2
	5.97 MPa @Strain 2.50 %, Temperature 80.0 °C	866 psi @Strain 2.50 %, Temperature 176 °F	ISO 11403-1/-2
	5.99 MPa @Strain 3.80 %, Temperature 120 °C	869 psi @Strain 3.80 %, Temperature 248 °F	ISO 11403-1/-2
	6.07 MPa @Strain 1.60 %, Temperature 60.0 °C	880 psi @Strain 1.60 %, Temperature 140 °F	ISO 11403-1/-2
	6.11 MPa @Strain 3.90 %, Temperature 120 °C	886 psi @Strain 3.90 %, Temperature 248 °F	ISO 11403-1/-2
	6.13 MPa @Strain 2.60 %, Temperature 80.0 °C	889 psi @Strain 2.60 %, Temperature 176 °F	ISO 11403-1/-2
	6.13 MPa @Strain 3.10 %, Temperature 100 °C	889 psi @Strain 3.10 %, Temperature 212 °F	ISO 11403-1/-2
	6.22 MPa @Strain 0.300 %, Temperature -40.0 °C	902 psi @Strain 0.300 %, Temperature -40.0 °F	ISO 11403-1/-2
	6.23 MPa @Strain 4.00 %, Temperature 120 °C	904 psi @Strain 4.00 %, Temperature 248 °F	ISO 11403-1/-2
	6.24 MPa @Strain 3.20 %, Temperature 100 °C	905 psi @Strain 3.20 %, Temperature 212 °F	ISO 11403-1/-2
	6.28 MPa @Strain 0.400 %, Temperature 23.0 °C	911 psi @Strain 0.400 %, Temperature 73.4 °F	ISO 11403-1/-2
	6.29 MPa @Strain 1.70 %, Temperature 60.0 °C	912 psi @Strain 1.70 %, Temperature 140 °F	ISO 11403-1/-2
	6.33 MPa @Strain 4.10 %, Temperature 120 °C	918 psi @Strain 4.10 %, Temperature 248 °F	ISO 11403-1/-2
	6.38 MPa @Strain 2.70 %, Temperature 80.0 °C	925 psi @Strain 2.70 %, Temperature 176 °F	ISO 11403-1/-2
	6.39 MPa @Strain 7.00 %, Temperature 150 °C	927 psi @Strain 7.00 %, Temperature 302 °F	ISO 11403-1/-2
	6.40 MPa @Strain 3.30 %, Temperature 100 °C	928 psi @Strain 3.30 %, Temperature 212 °F	ISO 11403-1/-2
	6.47 MPa @Strain 4.20 %, Temperature 120 °C	938 psi @Strain 4.20 %, Temperature 248 °F	ISO 11403-1/-2
	6.51 MPa @Strain 2.80 %, Temperature 80.0 °C	944 psi @Strain 2.80 %, Temperature 176 °F	ISO 11403-1/-2
	6.53 MPa @Strain 1.80 %, Temperature 60.0 °C	947 psi @Strain 1.80 %, Temperature 140 °F	ISO 11403-1/-2
	6.54 MPa @Strain 3.40 %, Temperature 100 °C	949 psi @Strain 3.40 %, Temperature 212 °F	ISO 11403-1/-2
	6.55 MPa @Strain 4.30 %, Temperature 120 °C	950 psi @Strain 4.30 %, Temperature 248 °F	ISO 11403-1/-2
	6.67 MPa @Strain 4.40 %, Temperature 120 °C	967 psi @Strain 4.40 %, Temperature 248 °F	ISO 11403-1/-2
	6.68 MPa @Strain 3.50 %, Temperature 100 °C	969 psi @Strain 3.50 %, Temperature 212 °F	ISO 11403-1/-2
	6.70 MPa @Strain 2.90 %, Temperature 80.0 °C	972 psi @Strain 2.90 %, Temperature 176 °F	ISO 11403-1/-2
	6.79 MPa @Strain 1.90 %, Temperature 60.0 °C	985 psi @Strain 1.90 %, Temperature 140 °F	ISO 11403-1/-2
	6.80 MPa @Strain 4.50 %, Temperature 120 °C	986 psi @Strain 4.50 %, Temperature 248 °F	ISO 11403-1/-2
	6.81 MPa @Strain 8.00 %, Temperature 150 °C	988 psi @Strain 8.00 %, Temperature 302 °F	ISO 11403-1/-2
	6.83 MPa @Strain 3.60 %, Temperature 100 °C	991 psi @Strain 3.60 %, Temperature 212 °F	ISO 11403-1/-2
	6.85 MPa @Strain 4.60 %, Temperature 120 °C	994 psi @Strain 4.60 %, Temperature 248 °F	ISO 11403-1/-2
	6.87 MPa @Strain 3.00 %, Temperature 80.0 °C	996 psi @Strain 3.00 %, Temperature 176 °F	ISO 11403-1/-2
	6.94 MPa @Strain 4.70 %, Temperature 120 °C	1010 psi @Strain 4.70 %, Temperature 248 °F	ISO 11403-1/-2
	6.98 MPa @Strain 3.70 %, Temperature 100 °C	1010 psi @Strain 3.70 %, Temperature 212 °F	ISO 11403-1/-2
	7.01 MPa @Strain 3.10 %, Temperature 80.0 °C	1020 psi @Strain 3.10 %, Temperature 176 °F	ISO 11403-1/-2
	7.03 MPa @Strain 3.09 %, Temperature 90.0 °C	1020 psi @Strain 3.09 %, Temperature 194 °F	ISO 527
	7.06 MPa @Strain 4.80 %, Temperature 120 °C	1020 psi @Strain 4.80 %, Temperature 248 °F	ISO 11403-1/-2
	7.11 MPa @Strain 2.00 %, Temperature 60.0 °C	1030 psi @Strain 2.00 %, Temperature 140 °F	ISO 11403-1/-2
	7.14 MPa @Strain 4.90 %, Temperature 120 °C	1040 psi @Strain 4.90 %, Temperature 248 °F	ISO 11403-1/-2
	7.14 MPa @Strain 3.80 %, Temperature 100 °C	1040 psi @Strain 3.80 %, Temperature 212 °F	ISO 11403-1/-2
	7.19 MPa @Strain 9.00 %, Temperature 150 °C	1040 psi @Strain 9.00 %, Temperature 302 °F	ISO 11403-1/-2
	7.22 MPa @Strain 3.90 %, Temperature 100 °C	1050 psi @Strain 3.90 %, Temperature 212 °F	ISO 11403-1/-2
	7.25 MPa @Strain 3.20 %, Temperature 80.0 °C	1050 psi @Strain 3.20 %, Temperature 176 °F	ISO 11403-1/-2
	7.26 MPa @Strain 5.00 %, Temperature 120 °C	1050 psi @Strain 5.00 %, Temperature 248 °F	ISO 11403-1/-2
	7.29 MPa @Strain 0.400 %, Temperature 0.000 °C	1060 psi @Strain 0.400 %, Temperature 32.0 °F	ISO 11403-1/-2
	7.33 MPa @Strain 4.00 %, Temperature 100 °C	1060 psi @Strain 4.00 %, Temperature 212 °F	ISO 11403-1/-2
	7.36 MPa @Strain 2.10 %, Temperature 60.0 °C	1070 psi @Strain 2.10 %, Temperature 140 °F	ISO 11403-1/-2
	7.38 MPa @Strain 3.30 %, Temperature 80.0 °C	1070 psi @Strain 3.30 %, Temperature 176 °F	ISO 11403-1/-2
	7.48 MPa @Strain 4.10 %, Temperature 100 °C	1080 psi @Strain 4.10 %, Temperature 212 °F	ISO 11403-1/-2
	7.53 MPa @Strain 3.40 %, Temperature 80.0 °C	1090 psi @Strain 3.40 %, Temperature 176 °F	ISO 11403-1/-2
	7.53 MPa @Strain 10.0 %, Temperature 150 °C	1090 psi @Strain 10.0 %, Temperature 302 °F	ISO 11403-1/-2
	7.62 MPa @Strain 4.20 %, Temperature 100 °C	1110 psi @Strain 4.20 %, Temperature 212 °F	ISO 11403-1/-2
	7.69 MPa @Strain 2.20 %, Temperature 60.0 °C	1120 psi @Strain 2.20 %, Temperature 140 °F	ISO 11403-1/-2
	7.73 MPa @Strain 4.30 %, Temperature 100 °C	1120 psi @Strain 4.30 %, Temperature 212 °F	ISO 11403-1/-2
	7.76 MPa @Strain 3.50 %, Temperature 80.0 °C	1130 psi @Strain 3.50 %, Temperature 176 °F	ISO 11403-1/-2
	7.82 MPa @Strain 4.40 %, Temperature 100 °C	1130 psi @Strain 4.40 %, Temperature 212 °F	ISO 11403-1/-2
	7.86 MPa @Strain 2.30 %, Temperature 60.0 °C	1140 psi @Strain 2.30 %, Temperature 140 °F	ISO 11403-1/-2
	7.87 MPa @Strain 3.60 %, Temperature 80.0 °C	1140 psi @Strain 3.60 %, Temperature 176 °F	ISO 11403-1/-2
	7.90 MPa @Strain 6.00 %, Temperature 120 °C	1150 psi @Strain 6.00 %, Temperature 248 °F	ISO 11403-1/-2
	7.98 MPa @Strain 4.50 %, Temperature 100 °C	1160 psi @Strain 4.50 %, Temperature 212 °F	ISO 11403-1/-2
	8.04 MPa @Strain 3.70 %, Temperature 80.0 °C	1170 psi @Strain 3.70 %, Temperature 176 °F	ISO 11403-1/-2
	8.10 MPa @Strain 4.60 %, Temperature 100 °C	1170 psi @Strain 4.60 %, Temperature 212 °F	ISO 11403-1/-2
	8.10 MPa @Strain 2.40 %, Temperature 60.0 °C	1170 psi @Strain 2.40 %, Temperature 140 °F	ISO 11403-1/-2
	8.17 MPa @Strain 4.70 %, Temperature 100 °C	1180 psi @Strain 4.70 %, Temperature 212 °F	ISO 11403-1/-2
	8.21 MPa @Strain 0.400 %, Temperature -40.0 °C	1190 psi @Strain 0.400 %, Temperature -40.0 °F	ISO 11403-1/-2
	8.23 MPa @Strain 3.80 %, Temperature 80.0 °C	1190 psi @Strain 3.80 %, Temperature 176 °F	ISO 11403-1/-2
	8.25 MPa @Strain 0.500 %, Temperature 23.0 °C	1200 psi @Strain 0.500 %, Temperature 73.4 °F	ISO 11403-1/-2
	8.32 MPa @Strain 4.80 %, Temperature 100 °C	1210 psi @Strain 4.80 %, Temperature 212 °F	ISO 11403-1/-2
	8.35 MPa @Strain 2.50 %, Temperature 60.0 °C	1210 psi @Strain 2.50 %, Temperature 140 °F	ISO 11403-1/-2
	8.36 MPa @Strain 3.90 %, Temperature 80.0 °C	1210 psi @Strain 3.90 %, Temperature 176 °F	ISO 11403-1/-2
	8.43 MPa @Strain 4.90 %, Temperature 100 °C	1220 psi @Strain 4.90 %, Temperature 212 °F	ISO 11403-1/-2
	8.52 MPa @Strain 4.00 %, Temperature 80.0 °C	1240 psi @Strain 4.00 %, Temperature 176 °F	ISO 11403-1/-2
	8.53 MPa @Strain 5.00 %, Temperature 100 °C	1240 psi @Strain 5.00 %, Temperature 212 °F	ISO 11403-1/-2
	8.57 MPa @Strain 15.0 %, Temperature 150 °C	1240 psi @Strain 15.0 %, Temperature 302 °F	ISO 11403-1/-2
	8.63 MPa @Strain 2.60 %, Temperature 60.0 °C	1250 psi @Strain 2.60 %, Temperature 140 °F	ISO 11403-1/-2
	8.64 MPa @Strain 4.10 %, Temperature 80.0 °C	1250 psi @Strain 4.10 %, Temperature 176 °F	ISO 11403-1/-2
	8.77 MPa @Strain 4.20 %, Temperature 80.0 °C	1270 psi @Strain 4.20 %, Temperature 176 °F	ISO 11403-1/-2
	8.82 MPa @Strain 2.70 %, Temperature 60.0 °C	1280 psi @Strain 2.70 %, Temperature 140 °F	ISO 11403-1/-2
	8.83 MPa @Strain 7.00 %, Temperature 120 °C	1280 psi @Strain 7.00 %, Temperature 248 °F	ISO 11403-1/-2
	8.97 MPa @Strain 4.30 %, Temperature 80.0 °C	1300 psi @Strain 4.30 %, Temperature 176 °F	ISO 11403-1/-2
	8.99 MPa @Strain 2.80 %, Temperature 60.0 °C	1300 psi @Strain 2.80 %, Temperature 140 °F	ISO 11403-1/-2
	9.07 MPa @Strain 4.40 %, Temperature 80.0 °C	1320 psi @Strain 4.40 %, Temperature 176 °F	ISO 11403-1/-2
	9.22 MPa @Strain 4.50 %, Temperature 80.0 °C	1340 psi @Strain 4.50 %, Temperature 176 °F	ISO 11403-1/-2
	9.26 MPa @Strain 2.90 %, Temperature 60.0 °C	1340 psi @Strain 2.90 %, Temperature 140 °F	ISO 11403-1/-2
	9.29 MPa @Strain 6.00 %, Temperature 100 °C	1350 psi @Strain 6.00 %, Temperature 212 °F	ISO 11403-1/-2
	9.38 MPa @Strain 4.60 %, Temperature 80.0 °C	1360 psi @Strain 4.60 %, Temperature 176 °F	ISO 11403-1/-2
	9.41 MPa @Strain 3.00 %, Temperature 60.0 °C	1360 psi @Strain 3.00 %, Temperature 140 °F	ISO 11403-1/-2
	9.46 MPa @Strain 8.00 %, Temperature 120 °C	1370 psi @Strain 8.00 %, Temperature 248 °F	ISO 11403-1/-2
	9.49 MPa @Strain 4.70 %, Temperature 80.0 °C	1380 psi @Strain 4.70 %, Temperature 176 °F	ISO 11403-1/-2
	9.49 MPa @Strain 0.500 %, Temperature 0.000 °C	1380 psi @Strain 0.500 %, Temperature 32.0 °F	ISO 11403-1/-2
	9.61 MPa @Strain 0.600 %, Temperature 23.0 °C	1390 psi @Strain 0.600 %, Temperature 73.4 °F	ISO 11403-1/-2
	9.62 MPa @Strain 3.10 %, Temperature 60.0 °C	1400 psi @Strain 3.10 %, Temperature 140 °F	ISO 11403-1/-2
	9.64 MPa @Strain 4.80 %, Temperature 80.0 °C	1400 psi @Strain 4.80 %, Temperature 176 °F	ISO 11403-1/-2
	9.70 MPa @Strain 20.0 %, Temperature 150 °C	1410 psi @Strain 20.0 %, Temperature 302 °F	ISO 11403-1/-2
	9.74 MPa @Strain 4.90 %, Temperature 80.0 °C	1410 psi @Strain 4.90 %, Temperature 176 °F	ISO 11403-1/-2
	9.84 MPa @Strain 3.20 %, Temperature 60.0 °C	1430 psi @Strain 3.20 %, Temperature 140 °F	ISO 11403-1/-2
	9.86 MPa @Strain 5.00 %, Temperature 80.0 °C	1430 psi @Strain 5.00 %, Temperature 176 °F	ISO 11403-1/-2
	9.88 MPa @Strain 0.500 %, Temperature -40.0 °C	1430 psi @Strain 0.500 %, Temperature -40.0 °F	ISO 11403-1/-2
	9.98 MPa @Strain 9.00 %, Temperature 120 °C	1450 psi @Strain 9.00 %, Temperature 248 °F	ISO 11403-1/-2
	10.02 MPa @Strain 3.30 %, Temperature 60.0 °C	1453 psi @Strain 3.30 %, Temperature 140 °F	ISO 11403-1/-2
	10.21 MPa @Strain 3.40 %, Temperature 60.0 °C	1481 psi @Strain 3.40 %, Temperature 140 °F	ISO 11403-1/-2
	10.3 MPa @Strain 7.00 %, Temperature 100 °C	1490 psi @Strain 7.00 %, Temperature 212 °F	ISO 11403-1/-2
	10.32 MPa @Strain 25.0 %, Temperature 150 °C	1497 psi @Strain 25.0 %, Temperature 302 °F	ISO 11403-1/-2
	10.4 MPa @Strain 3.50 %, Temperature 60.0 °C	1510 psi @Strain 3.50 %, Temperature 140 °F	ISO 11403-1/-2
	10.45 MPa @Strain 10.0 %, Temperature 120 °C	1516 psi @Strain 10.0 %, Temperature 248 °F	ISO 11403-1/-2
	10.61 MPa @Strain 3.60 %, Temperature 60.0 °C	1539 psi @Strain 3.60 %, Temperature 140 °F	ISO 11403-1/-2
	10.73 MPa @Strain 3.70 %, Temperature 60.0 °C	1556 psi @Strain 3.70 %, Temperature 140 °F	ISO 11403-1/-2
	10.76 MPa @Strain 6.00 %, Temperature 80.0 °C	1561 psi @Strain 6.00 %, Temperature 176 °F	ISO 11403-1/-2
	10.77 MPa @Strain 30.0 %, Temperature 150 °C	1562 psi @Strain 30.0 %, Temperature 302 °F	ISO 11403-1/-2
	10.8 MPa @Strain 6.13 %, Temperature 90.0 °C	1570 psi @Strain 6.13 %, Temperature 194 °F	ISO 527
	10.96 MPa @Strain 3.80 %, Temperature 60.0 °C	1590 psi @Strain 3.80 %, Temperature 140 °F	ISO 11403-1/-2
	10.97 MPa @Strain 0.700 %, Temperature 23.0 °C	1591 psi @Strain 0.700 %, Temperature 73.4 °F	ISO 11403-1/-2
	10.99 MPa @Strain 8.00 %, Temperature 100 °C	1594 psi @Strain 8.00 %, Temperature 212 °F	ISO 11403-1/-2
	11.03 MPa @Strain 0.600 %, Temperature 0.000 °C	1600 psi @Strain 0.600 %, Temperature 32.0 °F	ISO 11403-1/-2
	11.1 MPa @Strain 35.0 %, Temperature 150 °C	1610 psi @Strain 35.0 %, Temperature 302 °F	ISO 11403-1/-2
	11.12 MPa @Strain 3.90 %, Temperature 60.0 °C	1613 psi @Strain 3.90 %, Temperature 140 °F	ISO 11403-1/-2
	11.24 MPa @Strain 4.00 %, Temperature 60.0 °C	1630 psi @Strain 4.00 %, Temperature 140 °F	ISO 11403-1/-2
	11.37 MPa @Strain 40.0 %, Temperature 150 °C	1649 psi @Strain 40.0 %, Temperature 302 °F	ISO 11403-1/-2
	11.48 MPa @Strain 4.10 %, Temperature 60.0 °C	1665 psi @Strain 4.10 %, Temperature 140 °F	ISO 11403-1/-2
	11.59 MPa @Strain 4.20 %, Temperature 60.0 °C	1681 psi @Strain 4.20 %, Temperature 140 °F	ISO 11403-1/-2
	11.59 MPa @Strain 45.0 %, Temperature 150 °C	1681 psi @Strain 45.0 %, Temperature 302 °F	ISO 11403-1/-2
	11.6 MPa @Strain 9.00 %, Temperature 100 °C	1680 psi @Strain 9.00 %, Temperature 212 °F	ISO 11403-1/-2
	11.73 MPa @Strain 50.0 %, Temperature 150 °C	1701 psi @Strain 50.0 %, Temperature 302 °F	ISO 11403-1/-2
	11.75 MPa @Strain 0.600 %, Temperature -40.0 °C	1704 psi @Strain 0.600 %, Temperature -40.0 °F	ISO 11403-1/-2
	11.75 MPa @Strain 4.30 %, Temperature 60.0 °C	1704 psi @Strain 4.30 %, Temperature 140 °F	ISO 11403-1/-2
	11.79 MPa @Strain 15.0 %, Temperature 120 °C	1710 psi @Strain 15.0 %, Temperature 248 °F	ISO 11403-1/-2
	11.93 MPa @Strain 7.00 %, Temperature 80.0 °C	1730 psi @Strain 7.00 %, Temperature 176 °F	ISO 11403-1/-2
	11.93 MPa @Strain 4.40 %, Temperature 60.0 °C	1730 psi @Strain 4.40 %, Temperature 140 °F	ISO 11403-1/-2
	12.07 MPa @Strain 4.50 %, Temperature 60.0 °C	1751 psi @Strain 4.50 %, Temperature 140 °F	ISO 11403-1/-2
	12.09 MPa @Strain 10.0 %, Temperature 100 °C	1754 psi @Strain 10.0 %, Temperature 212 °F	ISO 11403-1/-2
	12.24 MPa @Strain 4.60 %, Temperature 60.0 °C	1775 psi @Strain 4.60 %, Temperature 140 °F	ISO 11403-1/-2
	12.31 MPa @Strain 0.800 %, Temperature 23.0 °C	1785 psi @Strain 0.800 %, Temperature 73.4 °F	ISO 11403-1/-2
	12.38 MPa @Strain 4.70 %, Temperature 60.0 °C	1796 psi @Strain 4.70 %, Temperature 140 °F	ISO 11403-1/-2
	12.52 MPa @Strain 0.700 %, Temperature 0.000 °C	1816 psi @Strain 0.700 %, Temperature 32.0 °F	ISO 11403-1/-2
	12.55 MPa @Strain 4.80 %, Temperature 60.0 °C	1820 psi @Strain 4.80 %, Temperature 140 °F	ISO 11403-1/-2
	12.66 MPa @Strain 4.90 %, Temperature 60.0 °C	1836 psi @Strain 4.90 %, Temperature 140 °F	ISO 11403-1/-2
	12.71 MPa @Strain 8.00 %, Temperature 80.0 °C	1843 psi @Strain 8.00 %, Temperature 176 °F	ISO 11403-1/-2
	12.83 MPa @Strain 5.00 %, Temperature 60.0 °C	1861 psi @Strain 5.00 %, Temperature 140 °F	ISO 11403-1/-2
	12.9 MPa @Strain 9.16 %, Temperature 90.0 °C	1870 psi @Strain 9.16 %, Temperature 194 °F	ISO 527
	13.12 MPa @Strain 20.0 %, Temperature 120 °C	1903 psi @Strain 20.0 %, Temperature 248 °F	ISO 11403-1/-2
	13.37 MPa @Strain 9.00 %, Temperature 80.0 °C	1939 psi @Strain 9.00 %, Temperature 176 °F	ISO 11403-1/-2
	13.49 MPa @Strain 15.0 %, Temperature 100 °C	1957 psi @Strain 15.0 %, Temperature 212 °F	ISO 11403-1/-2
	13.65 MPa @Strain 0.900 %, Temperature 23.0 °C	1980 psi @Strain 0.900 %, Temperature 73.4 °F	ISO 11403-1/-2
	13.67 MPa @Strain 0.700 %, Temperature -40.0 °C	1983 psi @Strain 0.700 %, Temperature -40.0 °F	ISO 11403-1/-2
	13.8 MPa @Strain 6.00 %, Temperature 60.0 °C	2000 psi @Strain 6.00 %, Temperature 140 °F	ISO 11403-1/-2
	13.8 MPa @Strain 25.0 %, Temperature 120 °C	2000 psi @Strain 25.0 %, Temperature 248 °F	ISO 11403-1/-2
	13.94 MPa @Strain 10.0 %, Temperature 80.0 °C	2022 psi @Strain 10.0 %, Temperature 176 °F	ISO 11403-1/-2
	14.06 MPa @Strain 0.800 %, Temperature 0.000 °C	2039 psi @Strain 0.800 %, Temperature 32.0 °F	ISO 11403-1/-2
	14.2 MPa @Strain 12.19 %, Temperature 90.0 °C	2060 psi @Strain 12.19 %, Temperature 194 °F	ISO 527
	14.28 MPa @Strain 30.0 %, Temperature 120 °C	2071 psi @Strain 30.0 %, Temperature 248 °F	ISO 11403-1/-2
	14.62 MPa @Strain 35.0 %, Temperature 120 °C	2120 psi @Strain 35.0 %, Temperature 248 °F	ISO 11403-1/-2
	14.86 MPa @Strain 20.0 %, Temperature 100 °C	2155 psi @Strain 20.0 %, Temperature 212 °F	ISO 11403-1/-2
	14.9 MPa @Strain 40.0 %, Temperature 120 °C	2160 psi @Strain 40.0 %, Temperature 248 °F	ISO 11403-1/-2
	14.94 MPa @Strain 1.00 %, Temperature 23.0 °C	2167 psi @Strain 1.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	15.08 MPa @Strain 7.00 %, Temperature 60.0 °C	2187 psi @Strain 7.00 %, Temperature 140 °F	ISO 11403-1/-2
	15.1 MPa @Strain 15.22 %, Temperature 90.0 °C	2190 psi @Strain 15.22 %, Temperature 194 °F	ISO 527
	15.12 MPa @Strain 45.0 %, Temperature 120 °C	2193 psi @Strain 45.0 %, Temperature 248 °F	ISO 11403-1/-2
	15.27 MPa @Strain 50.0 %, Temperature 120 °C	2215 psi @Strain 50.0 %, Temperature 248 °F	ISO 11403-1/-2
	15.49 MPa @Strain 15.0 %, Temperature 80.0 °C	2247 psi @Strain 15.0 %, Temperature 176 °F	ISO 11403-1/-2
	15.52 MPa @Strain 0.900 %, Temperature 0.000 °C	2251 psi @Strain 0.900 %, Temperature 32.0 °F	ISO 11403-1/-2
	15.53 MPa @Strain 25.0 %, Temperature 100 °C	2252 psi @Strain 25.0 %, Temperature 212 °F	ISO 11403-1/-2
	15.53 MPa @Strain 2.75 %, Temperature 40.0 °C	2252 psi @Strain 2.75 %, Temperature 104 °F	ISO 527
	15.56 MPa @Strain 0.800 %, Temperature -40.0 °C	2257 psi @Strain 0.800 %, Temperature -40.0 °F	ISO 11403-1/-2
	15.6 MPa @Strain 18.25 %, Temperature 90.0 °C	2260 psi @Strain 18.25 %, Temperature 194 °F	ISO 527
	15.93 MPa @Strain 8.00 %, Temperature 60.0 °C	2310 psi @Strain 8.00 %, Temperature 140 °F	ISO 11403-1/-2
	16.0 MPa @Strain 21.29 %, Temperature 90.0 °C	2320 psi @Strain 21.29 %, Temperature 194 °F	ISO 527
	16.01 MPa @Strain 30.0 %, Temperature 100 °C	2322 psi @Strain 30.0 %, Temperature 212 °F	ISO 11403-1/-2
	16.2 MPa @Strain 1.10 %, Temperature 23.0 °C	2350 psi @Strain 1.10 %, Temperature 73.4 °F	ISO 11403-1/-2
	16.3 MPa @Strain 24.32 %, Temperature 90.0 °C	2360 psi @Strain 24.32 %, Temperature 194 °F	ISO 527
	16.35 MPa @Strain 35.0 %, Temperature 100 °C	2371 psi @Strain 35.0 %, Temperature 212 °F	ISO 11403-1/-2
	16.5 MPa @Strain 27.35 %, Temperature 90.0 °C	2390 psi @Strain 27.35 %, Temperature 194 °F	ISO 527
	16.6 MPa @Strain 30.38 %, Temperature 90.0 °C	2410 psi @Strain 30.38 %, Temperature 194 °F	ISO 527
	16.62 MPa @Strain 40.0 %, Temperature 100 °C	2411 psi @Strain 40.0 %, Temperature 212 °F	ISO 11403-1/-2
	16.67 MPa @Strain 9.00 %, Temperature 60.0 °C	2418 psi @Strain 9.00 %, Temperature 140 °F	ISO 11403-1/-2
	16.86 MPa @Strain 45.0 %, Temperature 100 °C	2445 psi @Strain 45.0 %, Temperature 212 °F	ISO 11403-1/-2
	16.93 MPa @Strain 20.0 %, Temperature 80.0 °C	2455 psi @Strain 20.0 %, Temperature 176 °F	ISO 11403-1/-2
	16.99 MPa @Strain 1.00 %, Temperature 0.000 °C	2464 psi @Strain 1.00 %, Temperature 32.0 °F	ISO 11403-1/-2
	17.02 MPa @Strain 50.0 %, Temperature 100 °C	2469 psi @Strain 50.0 %, Temperature 212 °F	ISO 11403-1/-2
	17.28 MPa @Strain 10.0 %, Temperature 60.0 °C	2506 psi @Strain 10.0 %, Temperature 140 °F	ISO 11403-1/-2
	17.36 MPa @Strain 0.900 %, Temperature -40.0 °C	2518 psi @Strain 0.900 %, Temperature -40.0 °F	ISO 11403-1/-2
	17.46 MPa @Strain 1.20 %, Temperature 23.0 °C	2532 psi @Strain 1.20 %, Temperature 73.4 °F	ISO 11403-1/-2
	17.62 MPa @Strain 25.0 %, Temperature 80.0 °C	2556 psi @Strain 25.0 %, Temperature 176 °F	ISO 11403-1/-2
	18.07 MPa @Strain 30.0 %, Temperature 80.0 °C	2621 psi @Strain 30.0 %, Temperature 176 °F	ISO 11403-1/-2
	18.28 MPa @Strain 1.10 %, Temperature 0.000 °C	2651 psi @Strain 1.10 %, Temperature 32.0 °F	ISO 11403-1/-2
	18.42 MPa @Strain 35.0 %, Temperature 80.0 °C	2672 psi @Strain 35.0 %, Temperature 176 °F	ISO 11403-1/-2
	18.62 MPa @Strain 1.30 %, Temperature 23.0 °C	2701 psi @Strain 1.30 %, Temperature 73.4 °F	ISO 11403-1/-2
	18.7 MPa @Strain 40.0 %, Temperature 80.0 °C	2710 psi @Strain 40.0 %, Temperature 176 °F	ISO 11403-1/-2
	18.92 MPa @Strain 15.0 %, Temperature 60.0 °C	2744 psi @Strain 15.0 %, Temperature 140 °F	ISO 11403-1/-2
	18.93 MPa @Strain 45.0 %, Temperature 80.0 °C	2746 psi @Strain 45.0 %, Temperature 176 °F	ISO 11403-1/-2
	19.16 MPa @Strain 50.0 %, Temperature 80.0 °C	2779 psi @Strain 50.0 %, Temperature 176 °F	ISO 11403-1/-2
	19.17 MPa @Strain 1.00 %, Temperature -40.0 °C	2780 psi @Strain 1.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	19.75 MPa @Strain 1.40 %, Temperature 23.0 °C	2865 psi @Strain 1.40 %, Temperature 73.4 °F	ISO 11403-1/-2
	20.08 MPa @Strain 5.39 %, Temperature 40.0 °C	2912 psi @Strain 5.39 %, Temperature 104 °F	ISO 527
	20.38 MPa @Strain 1.20 %, Temperature 0.000 °C	2956 psi @Strain 1.20 %, Temperature 32.0 °F	ISO 11403-1/-2
	20.44 MPa @Strain 20.0 %, Temperature 60.0 °C	2965 psi @Strain 20.0 %, Temperature 140 °F	ISO 11403-1/-2
	20.82 MPa @Strain 1.50 %, Temperature 23.0 °C	3020 psi @Strain 1.50 %, Temperature 73.4 °F	ISO 11403-1/-2
	20.96 MPa @Strain 1.10 %, Temperature -40.0 °C	3040 psi @Strain 1.10 %, Temperature -40.0 °F	ISO 11403-1/-2
	21.15 MPa @Strain 25.0 %, Temperature 60.0 °C	3068 psi @Strain 25.0 %, Temperature 140 °F	ISO 11403-1/-2
	21.63 MPa @Strain 30.0 %, Temperature 60.0 °C	3137 psi @Strain 30.0 %, Temperature 140 °F	ISO 11403-1/-2
	21.85 MPa @Strain 1.60 %, Temperature 23.0 °C	3169 psi @Strain 1.60 %, Temperature 73.4 °F	ISO 11403-1/-2
	21.98 MPa @Strain 35.0 %, Temperature 60.0 °C	3188 psi @Strain 35.0 %, Temperature 140 °F	ISO 11403-1/-2
	22.25 MPa @Strain 40.0 %, Temperature 60.0 °C	3227 psi @Strain 40.0 %, Temperature 140 °F	ISO 11403-1/-2
	22.39 MPa @Strain 1.30 %, Temperature 0.000 °C	3247 psi @Strain 1.30 %, Temperature 32.0 °F	ISO 11403-1/-2
	22.46 MPa @Strain 8.04 %, Temperature 40.0 °C	3258 psi @Strain 8.04 %, Temperature 104 °F	ISO 527
	22.48 MPa @Strain 45.0 %, Temperature 60.0 °C	3260 psi @Strain 45.0 %, Temperature 140 °F	ISO 11403-1/-2
	22.57 MPa @Strain 1.20 %, Temperature -40.0 °C	3274 psi @Strain 1.20 %, Temperature -40.0 °F	ISO 11403-1/-2
	22.63 MPa @Strain 50.0 %, Temperature 60.0 °C	3282 psi @Strain 50.0 %, Temperature 140 °F	ISO 11403-1/-2
	22.81 MPa @Strain 1.70 %, Temperature 23.0 °C	3308 psi @Strain 1.70 %, Temperature 73.4 °F	ISO 11403-1/-2
	23.71 MPa @Strain 1.90 %, Temperature 23.0 °C	3439 psi @Strain 1.90 %, Temperature 73.4 °F	ISO 11403-1/-2
	23.72 MPa @Strain 1.40 %, Temperature 0.000 °C	3440 psi @Strain 1.40 %, Temperature 32.0 °F	ISO 11403-1/-2
	23.84 MPa @Strain 10.69 %, Temperature 40.0 °C	3458 psi @Strain 10.69 %, Temperature 104 °F	ISO 527
	24.32 MPa @Strain 1.30 %, Temperature -40.0 °C	3527 psi @Strain 1.30 %, Temperature -40.0 °F	ISO 11403-1/-2
	24.52 MPa @Strain 2.00 %, Temperature 23.0 °C	3556 psi @Strain 2.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	24.72 MPa @Strain 13.33 %, Temperature 40.0 °C	3585 psi @Strain 13.33 %, Temperature 104 °F	ISO 527
	25.04 MPa @Strain 1.50 %, Temperature 0.000 °C	3632 psi @Strain 1.50 %, Temperature 32.0 °F	ISO 11403-1/-2
	25.27 MPa @Strain 2.10 %, Temperature 23.0 °C	3665 psi @Strain 2.10 %, Temperature 73.4 °F	ISO 11403-1/-2
	25.34 MPa @Strain 15.98 %, Temperature 40.0 °C	3675 psi @Strain 15.98 %, Temperature 104 °F	ISO 527
	25.71 MPa @Strain 18.63 %, Temperature 40.0 °C	3729 psi @Strain 18.63 %, Temperature 104 °F	ISO 527
	25.95 MPa @Strain 2.20 %, Temperature 23.0 °C	3764 psi @Strain 2.20 %, Temperature 73.4 °F	ISO 11403-1/-2
	25.98 MPa @Strain 21.48 %, Temperature 40.0 °C	3768 psi @Strain 21.48 %, Temperature 104 °F	ISO 527
	26.03 MPa @Strain 1.40 %, Temperature -40.0 °C	3775 psi @Strain 1.40 %, Temperature -40.0 °F	ISO 11403-1/-2
	26.12 MPa @Strain 24.12 %, Temperature 40.0 °C	3788 psi @Strain 24.12 %, Temperature 104 °F	ISO 527
	26.21 MPa @Strain 26.77 %, Temperature 40.0 °C	3801 psi @Strain 26.77 %, Temperature 104 °F	ISO 527
	26.29 MPa @Strain 1.60 %, Temperature 0.000 °C	3813 psi @Strain 1.60 %, Temperature 32.0 °F	ISO 11403-1/-2
	26.56 MPa @Strain 2.30 %, Temperature 23.0 °C	3852 psi @Strain 2.30 %, Temperature 73.4 °F	ISO 11403-1/-2
	27.07 MPa @Strain 2.40 %, Temperature 23.0 °C	3926 psi @Strain 2.40 %, Temperature 73.4 °F	ISO 11403-1/-2
	27.54 MPa @Strain 1.70 %, Temperature 0.000 °C	3994 psi @Strain 1.70 %, Temperature 32.0 °F	ISO 11403-1/-2
	27.55 MPa @Strain 2.60 %, Temperature 23.0 °C	3996 psi @Strain 2.60 %, Temperature 73.4 °F	ISO 11403-1/-2
	27.68 MPa @Strain 1.50 %, Temperature -40.0 °C	4015 psi @Strain 1.50 %, Temperature -40.0 °F	ISO 11403-1/-2
	27.95 MPa @Strain 2.70 %, Temperature 23.0 °C	4054 psi @Strain 2.70 %, Temperature 73.4 °F	ISO 11403-1/-2
	28.3 MPa @Strain 2.80 %, Temperature 23.0 °C	4100 psi @Strain 2.80 %, Temperature 73.4 °F	ISO 11403-1/-2
	28.61 MPa @Strain 3.00 %, Temperature 23.0 °C	4150 psi @Strain 3.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	28.66 MPa @Strain 1.80 %, Temperature 0.000 °C	4157 psi @Strain 1.80 %, Temperature 32.0 °F	ISO 11403-1/-2
	28.88 MPa @Strain 3.10 %, Temperature 23.0 °C	4189 psi @Strain 3.10 %, Temperature 73.4 °F	ISO 11403-1/-2
	29.1 MPa @Strain 3.30 %, Temperature 23.0 °C	4220 psi @Strain 3.30 %, Temperature 73.4 °F	ISO 11403-1/-2
	29.28 MPa @Strain 1.60 %, Temperature -40.0 °C	4247 psi @Strain 1.60 %, Temperature -40.0 °F	ISO 11403-1/-2
	29.3 MPa @Strain 3.40 %, Temperature 23.0 °C	4250 psi @Strain 3.40 %, Temperature 73.4 °F	ISO 11403-1/-2
	29.49 MPa @Strain 3.50 %, Temperature 23.0 °C	4277 psi @Strain 3.50 %, Temperature 73.4 °F	ISO 11403-1/-2
	29.64 MPa @Strain 3.70 %, Temperature 23.0 °C	4299 psi @Strain 3.70 %, Temperature 73.4 °F	ISO 11403-1/-2
	29.78 MPa @Strain 3.80 %, Temperature 23.0 °C	4319 psi @Strain 3.80 %, Temperature 73.4 °F	ISO 11403-1/-2
	29.78 MPa @Strain 1.90 %, Temperature 0.000 °C	4319 psi @Strain 1.90 %, Temperature 32.0 °F	ISO 11403-1/-2
	29.93 MPa @Strain 4.00 %, Temperature 23.0 °C	4341 psi @Strain 4.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.02 MPa @Strain 4.10 %, Temperature 23.0 °C	4354 psi @Strain 4.10 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.14 MPa @Strain 4.30 %, Temperature 23.0 °C	4371 psi @Strain 4.30 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.25 MPa @Strain 4.40 %, Temperature 23.0 °C	4387 psi @Strain 4.40 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.35 MPa @Strain 4.60 %, Temperature 23.0 °C	4402 psi @Strain 4.60 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.43 MPa @Strain 4.70 %, Temperature 23.0 °C	4414 psi @Strain 4.70 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.53 MPa @Strain 4.90 %, Temperature 23.0 °C	4428 psi @Strain 4.90 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.62 MPa @Strain 5.00 %, Temperature 23.0 °C	4441 psi @Strain 5.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.84 MPa @Strain 2.00 %, Temperature 0.000 °C	4473 psi @Strain 2.00 %, Temperature 32.0 °F	ISO 11403-1/-2
	30.99 MPa @Strain 6.00 %, Temperature 23.0 °C	4495 psi @Strain 6.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	30.99 MPa @Strain 1.70 %, Temperature -40.0 °C	4495 psi @Strain 1.70 %, Temperature -40.0 °F	ISO 11403-1/-2
	31.0 MPa @Strain 25.0 %, Temperature 23.0 °C	4500 psi @Strain 25.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.37 MPa @Strain 50.0 %, Temperature 23.0 °C	4550 psi @Strain 50.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.44 MPa @Strain 30.0 %, Temperature 23.0 °C	4560 psi @Strain 30.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.45 MPa @Strain 7.00 %, Temperature 23.0 °C	4561 psi @Strain 7.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.46 MPa @Strain 45.0 %, Temperature 23.0 °C	4563 psi @Strain 45.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.58 MPa @Strain 40.0 %, Temperature 23.0 °C	4580 psi @Strain 40.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.72 MPa @Strain 8.00 %, Temperature 23.0 °C	4601 psi @Strain 8.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.87 MPa @Strain 35.0 %, Temperature 23.0 °C	4622 psi @Strain 35.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.91 MPa @Strain 2.10 %, Temperature 0.000 °C	4628 psi @Strain 2.10 %, Temperature 32.0 °F	ISO 11403-1/-2
	31.92 MPa @Strain 20.0 %, Temperature 23.0 °C	4630 psi @Strain 20.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	31.96 MPa @Strain 9.00 %, Temperature 23.0 °C	4635 psi @Strain 9.00 %, Temperature 73.4 °F	ISO 11403-1/-2
	32.13 MPa @Strain 10.0 %, Temperature 23.0 °C	4660 psi @Strain 10.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	32.35 MPa @Strain 15.0 %, Temperature 23.0 °C	4692 psi @Strain 15.0 %, Temperature 73.4 °F	ISO 11403-1/-2
	32.69 MPa @Strain 1.80 %, Temperature -40.0 °C	4741 psi @Strain 1.80 %, Temperature -40.0 °F	ISO 11403-1/-2
	32.85 MPa @Strain 2.20 %, Temperature 0.000 °C	4764 psi @Strain 2.20 %, Temperature 32.0 °F	ISO 11403-1/-2
	33.79 MPa @Strain 2.30 %, Temperature 0.000 °C	4901 psi @Strain 2.30 %, Temperature 32.0 °F	ISO 11403-1/-2
	34.2 MPa @Strain 1.90 %, Temperature -40.0 °C	4960 psi @Strain 1.90 %, Temperature -40.0 °F	ISO 11403-1/-2
	34.63 MPa @Strain 2.40 %, Temperature 0.000 °C	5023 psi @Strain 2.40 %, Temperature 32.0 °F	ISO 11403-1/-2
	35.44 MPa @Strain 2.50 %, Temperature 0.000 °C	5140 psi @Strain 2.50 %, Temperature 32.0 °F	ISO 11403-1/-2
	35.65 MPa @Strain 2.00 %, Temperature -40.0 °C	5171 psi @Strain 2.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	36.18 MPa @Strain 2.60 %, Temperature 0.000 °C	5247 psi @Strain 2.60 %, Temperature 32.0 °F	ISO 11403-1/-2
	36.87 MPa @Strain 2.70 %, Temperature 0.000 °C	5348 psi @Strain 2.70 %, Temperature 32.0 °F	ISO 11403-1/-2
	37.07 MPa @Strain 2.10 %, Temperature -40.0 °C	5377 psi @Strain 2.10 %, Temperature -40.0 °F	ISO 11403-1/-2
	37.5 MPa @Strain 2.80 %, Temperature 0.000 °C	5440 psi @Strain 2.80 %, Temperature 32.0 °F	ISO 11403-1/-2
	38.05 MPa @Strain 2.90 %, Temperature 0.000 °C	5519 psi @Strain 2.90 %, Temperature 32.0 °F	ISO 11403-1/-2
	38.41 MPa @Strain 2.20 %, Temperature -40.0 °C	5571 psi @Strain 2.20 %, Temperature -40.0 °F	ISO 11403-1/-2
	38.49 MPa @Strain 3.00 %, Temperature 0.000 °C	5583 psi @Strain 3.00 %, Temperature 32.0 °F	ISO 11403-1/-2
	38.92 MPa @Strain 3.10 %, Temperature 0.000 °C	5645 psi @Strain 3.10 %, Temperature 32.0 °F	ISO 11403-1/-2
	39.4 MPa @Strain 3.20 %, Temperature 0.000 °C	5710 psi @Strain 3.20 %, Temperature 32.0 °F	ISO 11403-1/-2
	39.7 MPa @Strain 2.30 %, Temperature -40.0 °C	5760 psi @Strain 2.30 %, Temperature -40.0 °F	ISO 11403-1/-2
	39.85 MPa @Strain 3.30 %, Temperature 0.000 °C	5780 psi @Strain 3.30 %, Temperature 32.0 °F	ISO 11403-1/-2
	40.31 MPa @Strain 3.40 %, Temperature 0.000 °C	5846 psi @Strain 3.40 %, Temperature 32.0 °F	ISO 11403-1/-2
	40.69 MPa @Strain 3.50 %, Temperature 0.000 °C	5902 psi @Strain 3.50 %, Temperature 32.0 °F	ISO 11403-1/-2
	41.06 MPa @Strain 3.70 %, Temperature 0.000 °C	5955 psi @Strain 3.70 %, Temperature 32.0 °F	ISO 11403-1/-2
	41.17 MPa @Strain 2.40 %, Temperature -40.0 °C	5971 psi @Strain 2.40 %, Temperature -40.0 °F	ISO 11403-1/-2
	41.33 MPa @Strain 3.80 %, Temperature 0.000 °C	5994 psi @Strain 3.80 %, Temperature 32.0 °F	ISO 11403-1/-2
	41.62 MPa @Strain 3.90 %, Temperature 0.000 °C	6036 psi @Strain 3.90 %, Temperature 32.0 °F	ISO 11403-1/-2
	41.66 MPa @Strain 20.0 %, Temperature 0.000 °C	6042 psi @Strain 20.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	41.84 MPa @Strain 4.10 %, Temperature 0.000 °C	6068 psi @Strain 4.10 %, Temperature 32.0 °F	ISO 11403-1/-2
	41.97 MPa @Strain 25.0 %, Temperature 0.000 °C	6087 psi @Strain 25.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.0 MPa @Strain 30.0 %, Temperature 0.000 °C	6090 psi @Strain 30.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.06 MPa @Strain 35.0 %, Temperature 0.000 °C	6100 psi @Strain 35.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.08 MPa @Strain 40.0 %, Temperature 0.000 °C	6103 psi @Strain 40.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.12 MPa @Strain 4.20 %, Temperature 0.000 °C	6109 psi @Strain 4.20 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.13 MPa @Strain 45.0 %, Temperature 0.000 °C	6110 psi @Strain 45.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.14 MPa @Strain 50.0 %, Temperature 0.000 °C	6112 psi @Strain 50.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.3 MPa @Strain 4.30 %, Temperature 0.000 °C	6140 psi @Strain 4.30 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.35 MPa @Strain 15.0 %, Temperature 0.000 °C	6142 psi @Strain 15.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.44 MPa @Strain 2.50 %, Temperature -40.0 °C	6155 psi @Strain 2.50 %, Temperature -40.0 °F	ISO 11403-1/-2
	42.5 MPa @Strain 4.50 %, Temperature 0.000 °C	6160 psi @Strain 4.50 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.63 MPa @Strain 4.60 %, Temperature 0.000 °C	6183 psi @Strain 4.60 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.78 MPa @Strain 4.80 %, Temperature 0.000 °C	6205 psi @Strain 4.80 %, Temperature 32.0 °F	ISO 11403-1/-2
	42.89 MPa @Strain 4.90 %, Temperature 0.000 °C	6221 psi @Strain 4.90 %, Temperature 32.0 °F	ISO 11403-1/-2
	43.45 MPa @Strain 6.00 %, Temperature 0.000 °C	6302 psi @Strain 6.00 %, Temperature 32.0 °F	ISO 11403-1/-2
	43.62 MPa @Strain 2.60 %, Temperature -40.0 °C	6327 psi @Strain 2.60 %, Temperature -40.0 °F	ISO 11403-1/-2
	43.85 MPa @Strain 10.0 %, Temperature 0.000 °C	6360 psi @Strain 10.0 %, Temperature 32.0 °F	ISO 11403-1/-2
	43.87 MPa @Strain 7.00 %, Temperature 0.000 °C	6363 psi @Strain 7.00 %, Temperature 32.0 °F	ISO 11403-1/-2
	43.96 MPa @Strain 9.00 %, Temperature 0.000 °C	6376 psi @Strain 9.00 %, Temperature 32.0 °F	ISO 11403-1/-2
	43.98 MPa @Strain 8.00 %, Temperature 0.000 °C	6379 psi @Strain 8.00 %, Temperature 32.0 °F	ISO 11403-1/-2
	44.86 MPa @Strain 2.70 %, Temperature -40.0 °C	6506 psi @Strain 2.70 %, Temperature -40.0 °F	ISO 11403-1/-2
	45.94 MPa @Strain 2.80 %, Temperature -40.0 °C	6663 psi @Strain 2.80 %, Temperature -40.0 °F	ISO 11403-1/-2
	46.84 MPa @Strain 2.90 %, Temperature -40.0 °C	6794 psi @Strain 2.90 %, Temperature -40.0 °F	ISO 11403-1/-2
	47.58 MPa @Strain 3.00 %, Temperature -40.0 °C	6901 psi @Strain 3.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	48.46 MPa @Strain 3.10 %, Temperature -40.0 °C	7029 psi @Strain 3.10 %, Temperature -40.0 °F	ISO 11403-1/-2
	49.3 MPa @Strain 3.20 %, Temperature -40.0 °C	7150 psi @Strain 3.20 %, Temperature -40.0 °F	ISO 11403-1/-2
	49.98 MPa @Strain 3.30 %, Temperature -40.0 °C	7249 psi @Strain 3.30 %, Temperature -40.0 °F	ISO 11403-1/-2
	50.61 MPa @Strain 3.40 %, Temperature -40.0 °C	7340 psi @Strain 3.40 %, Temperature -40.0 °F	ISO 11403-1/-2
	51.24 MPa @Strain 3.50 %, Temperature -40.0 °C	7432 psi @Strain 3.50 %, Temperature -40.0 °F	ISO 11403-1/-2
	51.87 MPa @Strain 3.60 %, Temperature -40.0 °C	7523 psi @Strain 3.60 %, Temperature -40.0 °F	ISO 11403-1/-2
	52.37 MPa @Strain 3.70 %, Temperature -40.0 °C	7596 psi @Strain 3.70 %, Temperature -40.0 °F	ISO 11403-1/-2
	52.88 MPa @Strain 3.80 %, Temperature -40.0 °C	7670 psi @Strain 3.80 %, Temperature -40.0 °F	ISO 11403-1/-2
	53.38 MPa @Strain 3.90 %, Temperature -40.0 °C	7742 psi @Strain 3.90 %, Temperature -40.0 °F	ISO 11403-1/-2
	53.84 MPa @Strain 4.00 %, Temperature -40.0 °C	7809 psi @Strain 4.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	54.29 MPa @Strain 4.10 %, Temperature -40.0 °C	7874 psi @Strain 4.10 %, Temperature -40.0 °F	ISO 11403-1/-2
	54.64 MPa @Strain 4.20 %, Temperature -40.0 °C	7925 psi @Strain 4.20 %, Temperature -40.0 °F	ISO 11403-1/-2
	54.89 MPa @Strain 30.0 %, Temperature -40.0 °C	7961 psi @Strain 30.0 %, Temperature -40.0 °F	ISO 11403-1/-2
	54.98 MPa @Strain 4.30 %, Temperature -40.0 °C	7974 psi @Strain 4.30 %, Temperature -40.0 °F	ISO 11403-1/-2
	55.41 MPa @Strain 4.40 %, Temperature -40.0 °C	8037 psi @Strain 4.40 %, Temperature -40.0 °F	ISO 11403-1/-2
	55.82 MPa @Strain 4.50 %, Temperature -40.0 °C	8096 psi @Strain 4.50 %, Temperature -40.0 °F	ISO 11403-1/-2
	56.16 MPa @Strain 4.60 %, Temperature -40.0 °C	8145 psi @Strain 4.60 %, Temperature -40.0 °F	ISO 11403-1/-2
	56.5 MPa @Strain 4.70 %, Temperature -40.0 °C	8190 psi @Strain 4.70 %, Temperature -40.0 °F	ISO 11403-1/-2
	56.73 MPa @Strain 4.80 %, Temperature -40.0 °C	8228 psi @Strain 4.80 %, Temperature -40.0 °F	ISO 11403-1/-2
	56.94 MPa @Strain 4.90 %, Temperature -40.0 °C	8258 psi @Strain 4.90 %, Temperature -40.0 °F	ISO 11403-1/-2
	57.23 MPa @Strain 5.00 %, Temperature -40.0 °C	8301 psi @Strain 5.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	57.26 MPa @Strain 25.0 %, Temperature -40.0 °C	8305 psi @Strain 25.0 %, Temperature -40.0 °F	ISO 11403-1/-2
	58.7 MPa @Strain 6.00 %, Temperature -40.0 °C	8510 psi @Strain 6.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	60.41 MPa @Strain 7.00 %, Temperature -40.0 °C	8762 psi @Strain 7.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	61.32 MPa @Strain 8.00 %, Temperature -40.0 °C	8894 psi @Strain 8.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	62.0 MPa @Strain 9.00 %, Temperature -40.0 °C	8990 psi @Strain 9.00 %, Temperature -40.0 °F	ISO 11403-1/-2
	62.44 MPa @Strain 10.0 %, Temperature -40.0 °C	9056 psi @Strain 10.0 %, Temperature -40.0 °F	ISO 11403-1/-2
	62.92 MPa @Strain 20.0 %, Temperature -40.0 °C	9126 psi @Strain 20.0 %, Temperature -40.0 °F	ISO 11403-1/-2
	63.58 MPa @Strain 15.0 %, Temperature -40.0 °C	9222 psi @Strain 15.0 %, Temperature -40.0 °F	ISO 11403-1/-2
Tensile Strength, Yield	38.0 MPa @Temperature 23.0 °C	5510 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	12 % @Temperature -40.0 °C	12 % @Temperature -40.0 °F	nominal; ISO 527
	14 % @Temperature -40.0 °C	14 % @Temperature -40.0 °F	ASTM D638
	>= 50 % @Temperature 23.0 °C	>= 50 % @Temperature 73.4 °F	nominal; ISO 527
	>= 50 % @Temperature 100 °C	>= 50 % @Temperature 212 °F	nominal; ISO 527
	145 % @Temperature 23.0 °C	145 % @Temperature 73.4 °F	ASTM D638
	150 % @Temperature 23.0 °C	150 % @Temperature 73.4 °F	50mm/min; ISO 527
	170 % @Temperature 90.0 °C	170 % @Temperature 194 °F	ASTM D638
	190 % @Temperature 150 °C	190 % @Temperature 302 °F	ASTM D638
Elongation at Yield	7.0 % @Temperature 23.0 °C	7.0 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	0.140 GPa @Temperature 150 °C	20.3 ksi @Temperature 302 °F	DAM; ISO 527
	0.177 GPa @Temperature 120 °C	25.7 ksi @Temperature 248 °F	DAM; ISO 527
	0.188 GPa @Temperature 100 °C	27.3 ksi @Temperature 212 °F	ISO 527
	0.244 GPa @Temperature 90.0 °C	35.4 ksi @Temperature 194 °F	DAM; ISO 527
	0.396 GPa @Temperature 60.0 °C	57.4 ksi @Temperature 140 °F	DAM; ISO 527
	0.807 GPa @Temperature 40.0 °C	117 ksi @Temperature 104 °F	DAM; ISO 527
	1.60 GPa @Temperature 23.0 °C	232 ksi @Temperature 73.4 °F	ASTM D638
	1.70 GPa @Temperature 23.0 °C	247 ksi @Temperature 73.4 °F	ISO 527
	1.863 GPa @Temperature 0.000 °C	270.2 ksi @Temperature 32.0 °F	DAM; ISO 527
	2.008 GPa @Temperature -20.0 °C	291.2 ksi @Temperature -4.00 °F	DAM; ISO 527
	2.14 GPa @Temperature -40.0 °C	310 ksi @Temperature -40.0 °F	ISO 527
	2.295 GPa @Temperature -40.0 °C	332.9 ksi @Temperature -40.0 °F	DAM; ISO 527
Flexural Strength	5.00 MPa @Temperature 149 °C	725 psi @Temperature 300 °F	ASTM D790
	8.40 MPa @Temperature 100 °C	1220 psi @Temperature 212 °F	ISO 178
	9.00 MPa @Temperature 90.0 °C	1310 psi @Temperature 194 °F	ASTM D790
	50.0 MPa @Temperature 23.0 °C	7250 psi @Temperature 73.4 °F	ISO 178
	53.0 MPa @Temperature 23.0 °C	7690 psi @Temperature 73.4 °F	ASTM D790
	73.4 MPa @Temperature -40.0 °C	10600 psi @Temperature -40.0 °F	ISO 178
	75.0 MPa @Temperature -40.0 °C	10900 psi @Temperature -40.0 °F	ASTM D790
Flexural Modulus	0.137 GPa @Temperature 149 °C	19.9 ksi @Temperature 300 °F	ASTM D790
	0.234 GPa @Temperature 90.0 °C	33.9 ksi @Temperature 194 °F	ASTM D790
	0.245 GPa @Temperature 100 °C	35.5 ksi @Temperature 212 °F	ISO 178
	1.55 GPa @Temperature 23.0 °C	225 ksi @Temperature 73.4 °F	ISO 178
	1.682 GPa @Temperature 23.0 °C	244.0 ksi @Temperature 73.4 °F	ASTM D790
	2.034 GPa @Temperature -40.0 °C	295.0 ksi @Temperature -40.0 °F	ASTM D790
	2.20 GPa @Temperature -40.0 °C	319 ksi @Temperature -40.0 °F	ISO 178
Compressive Strength	43.0 MPa @Temperature 23.0 °C	6240 psi @Temperature 73.4 °F	ASTM D695
Izod Impact, Notched	1.17 J/cm @Temperature -40.0 °C	2.19 ft-lb/in @Temperature -40.0 °F	ASTM D256
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ASTM D256
Izod Impact, Unnotched	NB @Temperature -40.0 °C	NB @Temperature -40.0 °F	ASTM D4812
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ASTM D4812
Izod Impact, Notched (ISO)	10.0 kJ/m2 @Temperature -40.0 °C	4.76 ft-lb/in2 @Temperature -40.0 °F	ISO 180/1A
	15.0 kJ/m2 @Temperature -30.0 °C	7.14 ft-lb/in2 @Temperature -22.0 °F	ISO 180/1A
	60.0 kJ/m2 @Temperature 23.0 °C	28.6 ft-lb/in2 @Temperature 73.4 °F	ISO 180/1A
Izod Impact, Unnotched (ISO)	270 kJ/m2 @Temperature -40.0 °C	128 ft-lb/in2 @Temperature -40.0 °F	ISO 180/1U
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 180/1U
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 180/1U
Charpy Impact Unnotched	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F	ISO 179/1eU
	NB @Temperature 23.0 °C	NB @Temperature 73.4 °F	ISO 179/1eU
Charpy Impact, Notched	1.00 J/cm2 @Temperature -40.0 °C	4.76 ft-lb/in2 @Temperature -40.0 °F	ISO 179/1eA
	1.00 J/cm2 @Temperature -30.0 °C	4.76 ft-lb/in2 @Temperature -22.0 °F	ISO 179/1eA
	8.50 J/cm2 @Temperature 23.0 °C	40.4 ft-lb/in2 @Temperature 73.4 °F	ISO 179/1eA
Tensile Creep Modulus, 1 hour	413 MPa @Temperature 23.0 °C, Time 3.60e+7 sec	59900 psi @Temperature 73.4 °F, Time 10000 hour	10MPa; ISO 899
	591 MPa @Temperature 23.0 °C, Time 3.60e+7 sec	85700 psi @Temperature 73.4 °F, Time 10000 hour	5MPa; ISO 899
	714 MPa @Temperature 23.0 °C, Time 3.60e+6 sec	104000 psi @Temperature 73.4 °F, Time 1000 hour	10MPa; ISO 899
	896 MPa @Temperature 23.0 °C, Time 3.60e+6 sec	130000 psi @Temperature 73.4 °F, Time 1000 hour	5MPa; ISO 899
	1070 MPa @Temperature 23.0 °C, Time 360000 sec	155000 psi @Temperature 73.4 °F, Time 100 hour	10MPa; ISO 899
	1180 MPa @Temperature 23.0 °C, Time 360000 sec	171000 psi @Temperature 73.4 °F, Time 100 hour	5MPa; ISO 899
	1360 MPa @Temperature 23.0 °C, Time 36000 sec	197000 psi @Temperature 73.4 °F, Time 10.0 hour	10MPa; ISO 899
	1410 MPa @Temperature 23.0 °C, Time 36000 sec	205000 psi @Temperature 73.4 °F, Time 10.0 hour	5MPa; ISO 899
	1500 MPa @Temperature 23.0 °C, Time 3600 sec	218000 psi @Temperature 73.4 °F, Time 1.00 hour	10MPa; ISO 899
	1540 MPa @Temperature 23.0 °C, Time 3600 sec	223000 psi @Temperature 73.4 °F, Time 1.00 hour	5MPa; ISO 899
	0.000 MPa @Strain 0.000 %, Temperature 23.0 °C	0.000 psi @Strain 0.000 %, Temperature 73.4 °F	10h; Isochronous; ISO 899
	0.000 MPa @Strain 0.000 %, Temperature 23.0 °C	0.000 psi @Strain 0.000 %, Temperature 73.4 °F	1h; Isochronous; ISO 899
	5.00 MPa @Strain 0.325 %, Temperature 23.0 °C	725 psi @Strain 0.325 %, Temperature 73.4 °F	1h; Isochronous; ISO 899
	5.00 MPa @Strain 0.355 %, Temperature 23.0 °C	725 psi @Strain 0.355 %, Temperature 73.4 °F	10h; Isochronous; ISO 899
	10.0 MPa @Strain 0.738 %, Temperature 23.0 °C	1450 psi @Strain 0.738 %, Temperature 73.4 °F	10h; Isochronous; ISO 899
	10.0 MPa @Strain 0.667 %, Temperature 23.0 °C	1450 psi @Strain 0.667 %, Temperature 73.4 °F	1h; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours	0.000 MPa @Strain 0.000 %, Temperature 23.0 °C	0.000 psi @Strain 0.000 %, Temperature 73.4 °F	10000h; Isochronous; ISO 899
	0.000 MPa @Strain 0.000 %, Temperature 23.0 °C	0.000 psi @Strain 0.000 %, Temperature 73.4 °F	1000h; Isochronous; ISO 899
	0.000 MPa @Strain 0.000 %, Temperature 23.0 °C	0.000 psi @Strain 0.000 %, Temperature 73.4 °F	100h; Isochronous; ISO 899
	5.00 MPa @Strain 0.423 %, Temperature 23.0 °C	725 psi @Strain 0.423 %, Temperature 73.4 °F	100h; Isochronous; ISO 899
	5.00 MPa @Strain 0.558 %, Temperature 23.0 °C	725 psi @Strain 0.558 %, Temperature 73.4 °F	1000h; Isochronous; ISO 899
	5.00 MPa @Strain 0.846 %, Temperature 23.0 °C	725 psi @Strain 0.846 %, Temperature 73.4 °F	10000h; Isochronous; ISO 899
	10.0 MPa @Strain 2.42 %, Temperature 23.0 °C	1450 psi @Strain 2.42 %, Temperature 73.4 °F	10000h; Isochronous; ISO 899
	10.0 MPa @Strain 1.40 %, Temperature 23.0 °C	1450 psi @Strain 1.40 %, Temperature 73.4 °F	1000h; Isochronous; ISO 899
	10.0 MPa @Strain 0.933 %, Temperature 23.0 °C	1450 psi @Strain 0.933 %, Temperature 73.4 °F	100h; Isochronous; ISO 899

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+15 ohm-cm @Temperature 23.0 °C	>= 1.00e+15 ohm-cm @Temperature 73.4 °F	IEC 60093
	1.00e+16 ohm-cm @Temperature 23.0 °C	1.00e+16 ohm-cm @Temperature 73.4 °F	ASTM D257
Surface Resistance	1.00e+14 ohm @Temperature 23.0 °C	1.00e+14 ohm @Temperature 73.4 °F	ASTM D257
	1.00e+15 ohm @Temperature 23.0 °C	1.00e+15 ohm @Temperature 73.4 °F	IEC 60093
Dielectric Constant	3.4 @Frequency 1.00e+6 Hz, Temperature 23.0 °C	3.4 @Frequency 1.00e+6 Hz, Temperature 73.4 °F	IEC 60250
	3.5 @Frequency 1000 Hz, Temperature 23.0 °C	3.5 @Frequency 1000 Hz, Temperature 73.4 °F	IEC 60250
	3.7 @Frequency 1.00e+6 Hz, Temperature 23.0 °C	3.7 @Frequency 1.00e+6 Hz, Temperature 73.4 °F	ASTM D150
	3.8 @Frequency 1000 Hz, Temperature 23.0 °C	3.8 @Frequency 1000 Hz, Temperature 73.4 °F	ASTM D150
Dielectric Strength	15.0 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C	381 kV/in @Thickness 0.126 in, Temperature 73.4 °F	Short Time; ASTM D149
	16.0 kV/mm @Thickness 2.00 mm, Temperature 150 °C	406 kV/in @Thickness 0.0787 in, Temperature 302 °F	IEC 60243-1
	21.0 kV/mm @Thickness 2.00 mm, Temperature 100 °C	533 kV/in @Thickness 0.0787 in, Temperature 212 °F	IEC 60243-1
	23.0 kV/mm @Thickness 1.60 mm, Temperature 23.0 °C	584 kV/in @Thickness 0.0630 in, Temperature 73.4 °F	Short Time; ASTM D149
	23.0 kV/mm @Thickness 2.00 mm, Temperature 23.0 °C	584 kV/in @Thickness 0.0787 in, Temperature 73.4 °F	IEC 60243-1
Dissipation Factor	0.0030 @Frequency 1000 Hz, Temperature 23.0 °C	0.0030 @Frequency 1000 Hz, Temperature 73.4 °F	ASTM D150
	0.0030 @Frequency 1000 Hz, Temperature 23.0 °C	0.0030 @Frequency 1000 Hz, Temperature 73.4 °F	IEC 60250
	0.019 @Frequency 1.00e+6 Hz, Temperature 23.0 °C	0.019 @Frequency 1.00e+6 Hz, Temperature 73.4 °F	IEC 60250
	0.020 @Frequency 100 Hz, Temperature 23.0 °C	0.020 @Frequency 100 Hz, Temperature 73.4 °F	IEC 60250
	0.021 @Frequency 1.00e+6 Hz, Temperature 23.0 °C	0.021 @Frequency 1.00e+6 Hz, Temperature 73.4 °F	ASTM D150
Comparative Tracking Index	600 V @Temperature 23.0 °C	600 V @Temperature 73.4 °F	IEC 60112

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	500 μm/m-°C @Temperature 23.0 - 55.0 °C	278 μin/in-°F @Temperature 73.4 - 131 °F	ASTM E 831
	500 μm/m-°C @Temperature 23.0 - 55.0 °C	278 μin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
CTE, linear, Transverse to Flow	190 μm/m-°C @Temperature 23.0 - 55.0 °C	106 μin/in-°F @Temperature 73.4 - 131 °F	ASTM E 831
	190 μm/m-°C @Temperature 23.0 - 55.0 °C	106 μin/in-°F @Temperature 73.4 - 131 °F	ISO 11359-1/-2
Melting Point	225 °C	437 °F	ASTM D3418
Deflection Temperature at 0.46 MPa (66 psi)	100 °C	212 °F	ISO 75-1/-2
	120 °C	248 °F	ASTM D648
	145 °C	293 °F	Annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	47.0 °C	117 °F	ASTM D648
	50.0 °C	122 °F	ISO 75-1/-2
UL RTI, Electrical	75.0 °C @Thickness 0.800 mm	167 °F @Thickness 0.0315 in	UL 746B
UL RTI, Mechanical with Impact	75.0 °C @Thickness 0.800 mm	167 °F @Thickness 0.0315 in	UL 746B
UL RTI, Mechanical without Impact	75.0 °C @Thickness 0.800 mm	167 °F @Thickness 0.0315 in	UL 746B
Flammability, UL94	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	IEC 60695-11-10
	HB @Thickness 0.800 mm	HB @Thickness 0.0315 in	UL94
Oxygen Index	19 %	19 %	ISO 4589-1/-2
	22 %	22 %	ASTM D2863
Glow Wire Test	700 °C @Thickness 3.00 mm	1290 °F @Thickness 0.118 in	IEC 60695-2-12

Processing Properties	Metric	English	Comments
Melt Temperature	225 °C	437 °F	10°C/min; ISO 11357-1/-3
	250 °C	482 °F	Optimum
	240 - 260 °C	464 - 500 °F
Mold Temperature	80.0 °C	176 °F	optimum
	30.0 - 130 °C	86.0 - 266 °F
Drying Temperature	110 - 130 °C	230 - 266 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Moisture Content	<= 0.040 %	<= 0.040 %

Descriptive Properties
Additive	Impact Modifier
	Lubricant
Appearance	Natural Color
Drying Recommended	Yes
Extrudable - Sheet	Yes
Extrudable - Tubing	Yes
Extrudable - Wire and Cable	Yes
Features	Chemical Resistance, Good
	Dimensional Stability, Good
	Elongation, Good
	Impact Resistance, High
	Moisture Absorption, Low
	Processability, Good
	Toughness, Good
Forms	Pellets
Generic	PBT
Material Status	Current
Part Marking Code	>PBT-HI<		ISO 11469
Polymer Family	Polyester
Polymer Type	PBT
Processing Method	Extrusion
	Injection Molding
Product Category	Extrusion Resins
	Toughened Resins
	Unreinforced Resins
Region Available - Global	Yes
Resin Identification	PBT-HI		ISO 1043
RoHS Compliance	Contact Manufacturer
Ultrasonic Weldable	Yes
Uses	Automotive Applications
	Industrial Applications
	Parts, Engineering

DuPont Performance Polymers Crastin? ST820 NC010 PBT