- 熔體流動速率 [g/10min]: 25.0
- 密度 [g/cm3]: 1.17
- 缺口沖擊強度: 7.47
- 拉伸強度 [MPa]: 51.7
- 斷裂伸長率 [%]: 72.4
- 彎曲模量 [MPa]: 1.86
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in3 | ASTM D792 | ||
| Melt Flow | 25 g/10 min @Load 5.00 kg, Temperature 260 °C | 25 g/10 min @Load 11.0 lb, Temperature 500 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 51.7 MPa | 7500 psi | ASTM D638 | ||
| Flexural Yield Strength | 72.4 MPa | 10500 psi | ASTM D790 | ||
| Flexural Modulus | 1.86 GPa | 270 ksi | ASTM D790 | ||
| Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | 73°F, 0.125 in; ASTM D256 | ||
| 4.81 J/cm @Temperature -50.0 °C | 9.00 ft-lb/in @Temperature -58.0 °F | 0.125 in; ASTM D256 | |||
| 5.34 J/cm @Temperature -40.0 °C | 10.0 ft-lb/in @Temperature -40.0 °F | 0.125 in; ASTM D256 | |||
| 6.14 J/cm @Temperature -30.0 °C | 11.5 ft-lb/in @Temperature -22.0 °F | 0.125 in; ASTM D256 | |||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 88.9 °C | 192 °F | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Rear Barrel Temperature | 243 - 266 °C | 470 - 510 °F | |||
| Middle Barrel Temperature | 249 - 271 °C | 480 - 520 °F | |||
| Front Barrel Temperature | 254 - 277 °C | 490 - 530 °F | |||
| Nozzle Temperature | 254 - 271 °C | 490 - 520 °F | |||
| Mold Temperature | 65.6 - 87.8 °C | 150 - 190 °F | |||
| Drying Temperature | 110 °C | 230 °F | |||
| Dry Time | 4 - 6 hour | 4 - 6 hour | |||
| Shot Size | 50 - 80 % | 50 - 80 % | |||
| Screw Speed | 50 - 80 rpm | 50 - 80 rpm | |||
| Descriptive Properties | |||||
| Injection Rate | Moderate | ||||