- 密度 [g/cm3]: 1.31
- 缺口沖擊強度: 0.53
- 拉伸強度 [MPa]: 52.0
- 斷裂伸長率 [%]: 83.0
- 彎曲模量 [MPa]: 2.30
- 熱變形溫度 [℃]: 154.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in3 | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.016 cm/cm | 0.0090 - 0.016 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 - 0.017 cm/cm | 0.010 - 0.017 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 52.0 MPa | 7540 psi | ASTM D638 |
| Flexural Yield Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm | 0.993 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 227 °C | 441 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 154 °C | 309 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM D648 |