- 熔體流動速率 [g/10min]: 30.0
- 缺口沖擊強度: 10.0
- 彎曲模量 [MPa]: 8.03
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 250 °C | 30 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 105 MPa | 15200 psi | ASTM D638 |
| Tensile Modulus | 8.70 GPa | 1260 ksi | ASTM D638 |
| Flexural Strength | 180 MPa | 26100 psi | ASTM D790 |
| Flexural Modulus | 8.03 GPa | 1160 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m2 | 4.76 ft-lb/in2 | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 62.0 kJ/m2 | 29.5 ft-lb/in2 | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.380 mm | HB @Thickness 0.0150 in | |
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||