- 熔體流動速率 [g/10min]: 18.0
- 缺口沖擊強度: 7.0
- 彎曲模量 [MPa]: 6.85
- 熱變形溫度 [℃]: 215.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.46 g/cc | 1.46 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.12 % | 0.12 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Melt Flow | 18 g/10 min @Load 2.16 kg, Temperature 250 °C | 18 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ASTM D638 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | ASTM D638 |
| Flexural Strength | 165 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 6.85 GPa | 994 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m2 | 3.33 ft-lb/in2 | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 43.0 kJ/m2 | 20.5 ft-lb/in2 | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 0.380 mm | HB @Thickness 0.0150 in | |
| HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | ||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||