- 熔體流動速率 [g/10min]: 16.83
- 密度 [g/cm3]: 1.53
- 吸水率 [%]: 0.4
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in3 | |||
| Density | 1.53 g/cc | 0.0553 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.40 % | 0.40 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | ISO 62 | ||
| Viscosity Measurement | 102 | 102 | [cm3/g]; ISO 307 | ||
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | plate with film gate 150x150x3mm3 | ||
| 0.0034 cm/cm | 0.0034 in/in | ISO 2577 | |||
| Linear Mold Shrinkage, Transverse | 0.0107 cm/cm | 0.0107 in/in | ISO 2577 | ||
| 0.011 cm/cm | 0.011 in/in | plate with film gate 150x150x3mm3 | |||
| Melt Flow | 16.83 g/10 min @Load 2.16 kg, Temperature 250 °C | 16.83 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Ball Indentation Hardness | 190 MPa @Load 98.0 kg, Time 30.0 sec | 27600 psi @Load 216 lb, Time 0.00833 hour | ISO 2039-1 | ||
| Tensile Strength at Break | 140 MPa | 20300 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 9.80 GPa | 1420 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 | ||
| Charpy Impact Unnotched | 7.00 J/cm2 @Temperature 23.0 °C | 33.3 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 0.950 J/cm2 @Temperature 23.0 °C | 4.52 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 7500 MPa @Strain <=0.500 % | 1.09e+6 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0025 @Frequency 100 Hz | 0.0025 @Frequency 100 Hz | IEC 60250 | ||
| 0.017 @Frequency 1.00e+6 Hz | 0.017 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 125 V | 125 V | Test Solution B; IEC 60112 | ||
| 375 V | 375 V | Test Solution A; IEC 60112 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.200 - 0.300 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.111 - 0.167 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft2-°F | DIN 52612-1 | ||
| Melting Point | 223 °C | 433 °F | ISO 11357-1/-2 | ||
| Maximum Service Temperature, Air | 140 °C | 284 °F | at 50% loss of tensile strength after 20,000hr | ||
| 160 °C | 320 °F | at 50% loss of tensile strength after 5,000hr | |||
| 210 °C | 410 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| HB @Diameter 4.00 mm | HB @Diameter 0.157 in | ||||
| HB @Diameter 0.400 mm | HB @Diameter 0.0157 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 275 °C | 482 - 527 °F | Injection molding/Extrusion | ||
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | Injection molding | ||
| Descriptive Properties | |||||
| Color | BK 15092 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 | |||