- 熔體流動速率 [g/10min]: 35.0
- 缺口沖擊強度: 9.0
- 彎曲模量 [MPa]: 7.50
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.56 g/cc | 1.56 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.17 % | 0.17 % | 50% RH; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ASTM D955 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 250 °C | 35 g/10 min @Load 4.76 lb, Temperature 482 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 110 MPa | 16000 psi | ASTM D638 |
| Flexural Strength | 175 MPa | 25400 psi | ASTM D790 |
| Flexural Modulus | 7.50 GPa | 1090 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m2 | 4.28 ft-lb/in2 | ASTM D256 |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m2 | 26.2 ft-lb/in2 | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm | V-0 @Thickness 0.0315 in | |
| V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | ||
| V-0 @Thickness 3.20 mm | V-0 @Thickness 0.126 in | ||