- 熔體流動速率 [g/10min]: 42.9
- 密度 [g/cm3]: 1.3
- 吸水率 [%]: 0.5
- 拉伸強度 [MPa]: 60.0
- 熱變形溫度 [℃]: 135.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.900 g/cc | 0.0217 - 0.0325 lb/in3 | |||
| Density | 1.30 g/cc | 0.0470 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.50 % | 0.50 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 0.25 % | 0.25 % | ISO 62 | ||
| Viscosity Measurement | 112 | 112 | [cm3/g]; ISO 307 | ||
| 70 @Temperature 290 °C | 70 @Temperature 554 °F | 20 mins plasticating | |||
| 75 @Temperature 280 °C | 75 @Temperature 536 °F | 30 mins plasticating | |||
| 75 @Temperature 300 °C | 75 @Temperature 572 °F | 10 mins plasticating | |||
| 90 @Temperature 270 °C | 90 @Temperature 518 °F | 30 mins plasticating | |||
| 95 @Temperature 290 °C | 95 @Temperature 554 °F | 10 mins plasticating | |||
| 100 @Temperature 260 °C | 100 @Temperature 500 °F | 30 mins plasticating | |||
| 100 @Temperature 300 °C | 100 @Temperature 572 °F | 5 mins plasticating | |||
| 105 @Temperature 280 °C | 105 @Temperature 536 °F | 10 mins plasticating | |||
| 106 @Temperature 250 °C | 106 @Temperature 482 °F | 30 mins plasticating | |||
| 110 @Temperature 270 °C | 110 @Temperature 518 °F | 10 mins plasticating | |||
| 115 @Temperature 260 °C | 115 @Temperature 500 °F | 10 mins plasticating | |||
| 115 @Temperature 240 °C | 115 @Temperature 464 °F | 30 mins plasticating | |||
| 117 @Temperature 250 °C | 117 @Temperature 482 °F | 10 mins plasticating | |||
| 120 @Temperature 240 °C | 120 @Temperature 464 °F | 10 mins plasticating | |||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | ISO 2577 | ||
| 0.015 cm/cm | 0.015 in/in | plate with film gate 150x150x3mm3 | |||
| Linear Mold Shrinkage, Transverse | 0.0164 cm/cm | 0.0164 in/in | ISO 2577 | ||
| 0.017 cm/cm | 0.017 in/in | plate with film gate 150x150x3mm3 | |||
| Melt Flow | 42.9 g/10 min @Load 2.16 kg, Temperature 250 °C | 42.9 g/10 min @Load 4.76 lb, Temperature 482 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min; ISO 527-1/-2 | ||
| 35 % | 35 % | Nominal Strain, 50 mm/min; ISO 527-1/-2 | |||
| Tensile Modulus | 2.60 GPa | 377 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 90.0 MPa | 13100 psi | ISO 178 | ||
| Charpy Impact Unnotched | 0.850 J/cm2 @Temperature -30.0 °C | 4.04 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | ||
| 14.0 J/cm2 @Temperature 23.0 °C | 66.6 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.380 J/cm2 @Temperature 23.0 °C | 1.81 ft-lb/in2 @Temperature 73.4 °F | ISO 179/1eA | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.3 @Frequency 1.00e+6 Hz | 3.3 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 3.4 @Frequency 100 Hz | 3.4 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.0020 @Frequency 100 Hz | 0.0020 @Frequency 100 Hz | IEC 60250 | ||
| 0.020 @Frequency 1.00e+6 Hz | 0.020 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 1.30 - 1.60 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.722 - 0.889 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Thermal Conductivity | 0.270 W/m-K | 1.87 BTU-in/hr-ft2-°F | DIN 52612-1 | ||
| Melting Point | 223 °C | 433 °F | ISO 11357-1/-2 | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Decomposition Temperature | >= 290 °C | >= 554 °F | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 250 °C | 482 °F | Feeding zone | ||
| Zone 2 | 255 °C | 491 °F | Compression | ||
| Zone 3 | 260 °C | 500 °F | Metering-zone | ||
| Zone 4 | 260 °C | 500 °F | Nozzle | ||
| Melt Temperature | 230 - 275 °C | 446 - 527 °F | Injection molding/Extrusion | ||
| 260 °C | 500 °F | Optimal | |||
| Mold Temperature | 40.0 - 70.0 °C | 104 - 158 °F | Injection molding | ||
| 60.0 °C | 140 °F | Optimal | |||
| Drying Temperature | 80.0 - 120 °C | 176 - 248 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Descriptive Properties | |||||
| Commercial Status | Europe | ||||
| Ignition Temperature | 350°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.25 m/s | ||||