- 拉伸強度 [MPa]: 26.17
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 78 | 78 | |
| Tensile Strength, Yield | 26.17 MPa | 3795 psi | |
| Elongation at Yield | 447 % | 447 % | |
| 100% Modulus | 0.00470 GPa | 0.682 ksi | |
| 200% Modulus | 0.009349 GPa | 1.356 ksi | |
| 300% Modulus | 0.01482 GPa | 2.149 ksi | |
| Tear Strength | 66.5 kN/m | 379 pli | Die C |
| Compression Set | 62 % @Temperature 70.0 °C, Time 79200 sec | 62 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 27.0 min @Temperature 154 °C | 0.450 hour @Temperature 310 °F | Press cured |