- 拉伸強度 [MPa]: 16.57
- 脆化溫度 [℃]: -58.0
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 50 | 50 | |
| Tensile Strength, Yield | 16.57 MPa | 2404 psi | |
| Elongation at Yield | 467 % | 467 % | |
| 100% Modulus | 0.00151 GPa | 0.219 ksi | |
| 200% Modulus | 0.00371 GPa | 0.538 ksi | |
| 300% Modulus | 0.007894 GPa | 1.145 ksi | |
| Tear Strength | 32.4 kN/m | 185 pli | Die C |
| Thermal Properties | Metric | English | Comments |
| Brittleness Temperature | -58.0 °C | -72.4 °F | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 35.0 min @Temperature 154 °C | 0.583 hour @Temperature 310 °F | |