- 拉伸強度 [MPa]: 14.35
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 67 | 67 | |
| Tensile Strength, Yield | 14.35 MPa | 2081 psi | |
| Elongation at Yield | 470 % | 470 % | |
| 100% Modulus | 0.00353 GPa | 0.512 ksi | |
| 200% Modulus | 0.00486 GPa | 0.705 ksi | |
| 300% Modulus | 0.00631 GPa | 0.915 ksi | |
| Tear Strength | 32.2 kN/m | 184 pli | Die C |
| Compression Set | 68 % @Temperature 70.0 °C, Time 79200 sec | 68 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 23.0 min @Temperature 154 °C | 0.383 hour @Temperature 310 °F | Press cured |