- 拉伸強度 [MPa]: 22.39
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 94 | 94 | |
| Tensile Strength, Yield | 22.39 MPa | 3247 psi | |
| Elongation at Yield | 232 % | 232 % | |
| 100% Modulus | 0.01495 GPa | 2.169 ksi | |
| 200% Modulus | 0.02134 GPa | 3.095 ksi | |
| Tear Strength | 64.1 kN/m | 366 pli | Die C |
| Taber Abrasion, mg/1000 Cycles | 0.24 | 0.24 | H-18, mg loss/rev |
| Compression Set | 56 % @Temperature 70.0 °C, Time 79200 sec | 56 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 20.0 min @Temperature 149 °C | 0.333 hour @Temperature 300 °F | |