- 拉伸強度 [MPa]: 25.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 63 | 63 | |
| Tensile Strength, Yield | 25.90 MPa | 3757 psi | |
| Elongation at Yield | 478 % | 478 % | |
| 100% Modulus | 0.00232 GPa | 0.336 ksi | |
| 200% Modulus | 0.00494 GPa | 0.716 ksi | |
| 300% Modulus | 0.009011 GPa | 1.307 ksi | |
| Tear Strength | 41.7 kN/m | 238 pli | Die C |
| Compression Set | 59 % @Temperature 70.0 °C, Time 79200 sec | 59 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 24.0 min @Temperature 154 °C | 0.400 hour @Temperature 310 °F | Press cured |