- 拉伸強度 [MPa]: 33.8
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |||
| Tensile Strength, Yield | 33.8 MPa | 4900 psi | |||
| Elongation at Yield | 620 % | 620 % | |||
| 100% Modulus | 0.00190 GPa | 0.275 ksi | |||
| 300% Modulus | 0.00931 GPa | 1.35 ksi | |||
| Tear Strength | 43.8 kN/m | 250 pli | Graves | ||
| Abrasion | 300 | 300 | NBS Index | ||
| Compression Set | 35 % @Temperature 70.0 °C, Time 79200 sec | 35 % @Temperature 158 °F, Time 22.0 hour | Method B | ||
| Processing Properties | Metric | English | Comments | ||
| Cure Time | 30.0 min @Temperature 154 °C | 0.500 hour @Temperature 310 °F | |||
| Descriptive Properties | |||||
| 500% Modulus (ksi) | 4.9 | ||||
| Mooney Scorch | >= 30 | at 250oF; >30 minutes to a 10 point rise | |||