- 拉伸強度 [MPa]: 33.87
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 33.87 MPa | 4912 psi | |
| Elongation at Yield | 559 % | 559 % | |
| 100% Modulus | 0.00423 GPa | 0.614 ksi | |
| 200% Modulus | 0.009735 GPa | 1.412 ksi | |
| 300% Modulus | 0.01668 GPa | 2.419 ksi | |
| Tear Strength | 60.0 kN/m | 342 pli | Die C |
| Compression Set | 34.6 % @Temperature 70.0 °C, Time 79200 sec | 34.6 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 8.40 min @Temperature 155 °C | 0.140 hour @Temperature 311 °F | TC90 |