- 拉伸強度 [MPa]: 30.55
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 30.55 MPa | 4431 psi | |
| Elongation at Yield | 546 % | 546 % | |
| 100% Modulus | 0.00371 GPa | 0.538 ksi | |
| 200% Modulus | 0.008515 GPa | 1.235 ksi | |
| 300% Modulus | 0.01467 GPa | 2.127 ksi | |
| Tear Strength | 60.1 kN/m | 343 pli | Die C |
| Compression Set | 29 % @Temperature 70.0 °C, Time 79200 sec | 29 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 6.30 min @Temperature 155 °C | 0.105 hour @Temperature 311 °F | TC90 |