- 拉伸強度 [MPa]: 32.76
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 70 | 70 | |
| Tensile Strength, Yield | 32.76 MPa | 4751 psi | |
| Elongation at Yield | 554 % | 554 % | |
| 100% Modulus | 0.00372 GPa | 0.539 ksi | |
| 200% Modulus | 0.008487 GPa | 1.231 ksi | |
| 300% Modulus | 0.01489 GPa | 2.159 ksi | |
| Tear Strength | 61.3 kN/m | 350 pli | Die C |
| Compression Set | 32.9 % @Temperature 70.0 °C, Time 79200 sec | 32.9 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 7.80 min @Temperature 155 °C | 0.130 hour @Temperature 311 °F | TC90 |