- 拉伸強度 [MPa]: 34.9
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 65 | 65 | |
| Tensile Strength, Yield | 34.9 MPa | 5060 psi | |
| Elongation at Yield | 690 % | 690 % | |
| 100% Modulus | 0.00269 GPa | 0.390 ksi | |
| 200% Modulus | 0.00572 GPa | 0.830 ksi | |
| 300% Modulus | 0.0103 GPa | 1.50 ksi | |
| Tear Strength | 56.0 kN/m | 320 pli | Die C |
| Compression Set | 36 % @Temperature 70.0 °C, Time 79200 sec | 36 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 2.40 min @Temperature 155 °C | 0.0400 hour @Temperature 311 °F | ts2 |
| 5.00 min @Temperature 155 °C | 0.0833 hour @Temperature 311 °F | TC90 | |