- 拉伸強度 [MPa]: 33.45
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 72 | 72 | |
| Tensile Strength, Yield | 33.45 MPa | 4852 psi | |
| Elongation at Yield | 562 % | 562 % | |
| 100% Modulus | 0.00394 GPa | 0.571 ksi | |
| 200% Modulus | 0.008915 GPa | 1.293 ksi | |
| 300% Modulus | 0.01546 GPa | 2.243 ksi | |
| Tear Strength | 61.8 kN/m | 353 pli | Die C |
| Compression Set | 38.4 % @Temperature 70.0 °C, Time 79200 sec | 38.4 % @Temperature 158 °F, Time 22.0 hour | |
| Processing Properties | Metric | English | Comments |
| Cure Time | 8.00 min @Temperature 155 °C | 0.133 hour @Temperature 311 °F | TC90 |