- 彎曲強(qiáng)度 [MPa]: 20.0
- 脆化溫度 [℃]: -37.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 83 @Temperature 100 °C | 83 @Temperature 212 °F | ML 1+4. ?Stock property.; ASTM D1646-81 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 70 | 70 | ASTM D2240-81 |
| Tensile Strength, Ultimate | 20.0 MPa | 2900 psi | ASTM D412-80 |
| Elongation at Break | 530 % | 530 % | ASTM D412-80 |
| 100% Modulus | 0.00530 GPa | 0.769 ksi | ASTM D412-80 |
| Resilience | 75 | 75 | % Yerzley; ASTM D945-77 |
| Tear Strength Test | 324 | 324 | lb-in. Graves Die C; ASTM D642-54 |
| Abrasion | 247 | 247 | NBS Abrasion Index; ASTM D1630-74. |
| Compression Set | 47 % @Temperature 70.0 °C | 47 % @Temperature 158 °F | 22 hr at 70°C. Method B. ASTM D395-69 |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -37.0 °C | -34.6 °F | Brittleness Temperature |
| Brittleness Temperature | -37.0 °C | -34.6 °F | ASTM D746-79 |
| Clash Berg Stiffness Temperature | -25.0 °C | -13.0 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |