- 彎曲強度 [MPa]: 20.7
- 脆化溫度 [℃]: -34.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Mooney Viscosity | 73 @Temperature 100 °C | 73 @Temperature 212 °F | ML 1+4. ?Stock property.; ASTM D1646-81 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore A | 69 | 69 | ASTM D2240-81 |
| Tensile Strength, Ultimate | 20.7 MPa | 3000 psi | ASTM D412-80 |
| Elongation at Break | 520 % | 520 % | ASTM D412-80 |
| 100% Modulus | 0.00600 GPa | 0.870 ksi | ASTM D412-80 |
| Resilience | 65 | 65 | % Yerzley; ASTM D945-77 |
| Tear Strength Test | 337 | 337 | lb-in. Graves Die C; ASTM D642-54 |
| Abrasion | 203 | 203 | NBS Abrasion Index; ASTM D1630-74. |
| Compression Set | 54 % @Temperature 70.0 °C | 54 % @Temperature 158 °F | 22 hr at 70°C. Method B. ASTM D395-69 |
| Thermal Properties | Metric | English | Comments |
| Minimum Service Temperature, Air | -34.0 °C | -29.2 °F | Brittleness Temperature |
| Brittleness Temperature | -34.0 °C | -29.2 °F | ASTM D746-79 |
| Clash Berg Stiffness Temperature | -26.0 °C | -14.8 °F | T-10000 Torsional stiffness ASTM D1043-72(1981) |