3M Dyneon? LTFE 6400ZC Low Temperature Fluoroelastomer

3M Dyneon? LTFE 6400ZC Low Temperature Fluoroelastomer 物性表: 3M Dyneon? LTFE 6400ZC Low Temperature Fluoroelastomer物性表及特性介紹,3M Dyneon? LTFE 6400ZC Low Temperature Fluoroelastomer注塑參數(shù)詳情,如需3M Dyneon? LTFE 6400ZC Low Temperature Fluoroelastomer下載, 可到相關(guān)下載區(qū)下載

脆化溫度 [℃]: -60.0

Physical Properties	Metric	English	Comments

Specific Gravity	1.86 g/cc	1.86 g/cc
Mooney Viscosity	95 @Temperature 121 °C	95 @Temperature 250 °F	ML 1+ 10

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	68	68	Press Cure 10 Minutes @ 177°C
	70	70	Post Cure 16 Hours @ 230°C
Tensile Strength at Break	11.9 MPa	1730 psi	Press Cure 10 Minutes @ 177°C
	13.3 MPa	1930 psi	Post Cure 16 Hours @ 230°C
Elongation at Break	175 %	175 %	Post Cure 16 Hours @ 230°C
	180 %	180 %	Press Cure 10 Minutes @ 177°C
100% Modulus	0.00610 GPa	0.885 ksi	Press Cure 10 Minutes @ 177°C
	0.00610 GPa	0.885 ksi	Post Cure 16 Hours @ 230°C
Compression Set	15 % @Treatment Temp. 150 °C, Time 252000 sec	15 % @Treatment Temp. 302 °F, Time 70.0 hour	Method B, -214 O-rings, Aged 70 Hours; ASTM D395
	26 % @Treatment Temp. 200 °C, Time 252000 sec	26 % @Treatment Temp. 392 °F, Time 70.0 hour	Method B, -214 O-rings, Aged 70 Hours; ASTM D395
	32 % @Treatment Temp. 200 °C, Time 605000 sec	32 % @Treatment Temp. 392 °F, Time 168 hour	Method B, -214 O-rings, Aged 168 Hours; ASTM D395

Thermal Properties	Metric	English	Comments
Minimum Service Temperature, Air	-40.0 °C	-40.0 °F	TR10
Brittleness Temperature	-60.0 °C	-76.0 °F
Glass Transition Temp, Tg	-40.0 °C	-40.0 °F
Transformation Temperature	-40.0 °C	-40.0 °F	TR10; ASTM D1329

Component Elements Properties	Metric	English	Comments
Fluorine, F	67.1 %	67.1 %

Descriptive Properties
Color	White
Form	Crumb
MH, Maximum Toque	14.0 Inch-lb		100 cpm, 0.5° Arc, 6 Minutes @ 177°C
ML, Minimum Torque	4.0 Inch-lb		100 cpm, 0.5° Arc, 6 Minutes @ 177°C
t², Time to 2 Inch-lb Rise from Minimum	0.5 Minutes		100 cpm, 0.5° Arc, 6 Minutes @ 177°C
t'50, Time to 50% Cure	0.7 Minutes		100 cpm, 0.5° Arc, 6 Minutes @ 177°C
t'90, Time to 90% Cure	2.3 Minutes		100 cpm, 0.5° Arc, 6 Minutes @ 177°C

關(guān)鍵詞:
TSE
供應(yīng)
3M Dyneon? LTFE 6400ZC Low Temperature Fluoroelastomer

轉(zhuǎn)載請(qǐng)注明: 轉(zhuǎn)自中國(guó)塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-36494.html

免責(zé)聲明: 本文 3M Dyneon? LTFE 6400ZC Low Temperature Fluoroelastomer 僅代表作者個(gè)人觀點(diǎn)，中國(guó)塑膠原料之家無(wú)關(guān)。中國(guó)塑膠原料之家網(wǎng)所轉(zhuǎn)載的內(nèi)容，其版權(quán)均由原作者和資料提供方所擁有！如因作品版權(quán)問(wèn)題需要處理，請(qǐng)與我們聯(lián)絡(luò)