- 脆化溫度 [℃]: -35.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.00 g/cc | 2.00 g/cc | |||
| Mooney Viscosity | 80 @Temperature 121 °C | 80 @Temperature 250 °F | ML 1+ 10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 72 | 72 | Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 200°C; ASTM D2240 | ||
| Tensile Strength at Break | 11.0 MPa | 1600 psi | Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 200°C; ASTM D412 | ||
| Elongation at Break | 230 % | 230 % | Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 200°C; ASTM D412 | ||
| 100% Modulus | 0.00480 GPa | 0.696 ksi | Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 200°C; ASTM D412 | ||
| Compression Set | 49 % @Treatment Temp. 200 °C, Time 252000 sec | 49 % @Treatment Temp. 392 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours, 25% Deformation; ASTM D395 | ||
| 69 % @Treatment Temp. 200 °C, Time 605000 sec | 69 % @Treatment Temp. 392 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 200 °C | 392 °F | |||
| Brittleness Temperature | -35.0 °C | -31.0 °F | |||
| Transformation Temperature | -2.00 °C | 28.4 °F | TR10 | ||
| Descriptive Properties | |||||
| Color | Off White | ||||
| Form | Slab | ||||
| MH, Maximum Toque | 11.9 Inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| ML, Minimum Torque | 2.0 Inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 0.8 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t'50, Time to 50% Cure | 1.1 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||
| t'90, Time to 90% Cure | 2.7 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D5289 | |||