- 脆化溫度 [℃]: -35.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 2.00 g/cc | 2.00 g/cc | |||
| Mooney Viscosity | 98 @Temperature 121 °C | 98 @Temperature 250 °F | ML 1+ 10 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 75 | 75 | Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D2240 | ||
| Tensile Strength at Break | 21.2 MPa | 3070 psi | Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D412 | ||
| Elongation at Break | 155 % | 155 % | Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D412 | ||
| 100% Modulus | 0.0106 GPa | 1.54 ksi | Press Cure 10 Minutes @ 177°C, Post Cure 16 Hours @ 232°C; ASTM D412 | ||
| Compression Set | 37 % @Treatment Temp. 230 °C, Time 252000 sec | 37 % @Treatment Temp. 446 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours, 25% Deformation; ASTM D395 | ||
| 40 % @Treatment Temp. 200 °C, Time 252000 sec | 40 % @Treatment Temp. 392 °F, Time 70.0 hour | Method B, -214 O-rings, Aged 70 Hours, 25% Deformation; ASTM D395 | |||
| 49 % @Treatment Temp. 200 °C, Time 605000 sec | 49 % @Treatment Temp. 392 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395 | |||
| 50 % @Treatment Temp. 230 °C, Time 605000 sec | 50 % @Treatment Temp. 446 °F, Time 168 hour | Method B, -214 O-rings, Aged 168 Hours, 25% Deformation; ASTM D395 | |||
| Thermal Properties | Metric | English | Comments | ||
| Maximum Service Temperature, Air | 220 °C | 428 °F | |||
| Brittleness Temperature | -35.0 °C | -31.0 °F | |||
| Transformation Temperature | -2.00 °C | 28.4 °F | TR10 | ||
| Descriptive Properties | |||||
| Color | White | ||||
| Form | Crumb | ||||
| MH, Maximum Toque | 16.0 Inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D412 | |||
| ML, Minimum Torque | 2.0 Inch-lb | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D412 | |||
| t2, Time to 2 Inch-lb Rise from Minimum | 0.5 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D412 | |||
| t'50, Time to 50% Cure | 0.7 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D412 | |||
| t'90, Time to 90% Cure | 1.7 Minutes | 100 cpm, 0.5° Arc, 6 Minutes @ 177°C, ASTM D412 | |||