- 密度 [g/cm3]: 1.68
- 吸水率 [%]: 0.05
- 彎曲模量 [MPa]: 13.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.670 g/cc | 0.0242 lb/in3 | ISO 60 | ||
| Density | 1.68 g/cc | 0.0607 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.050 % | 0.050 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0036 cm/cm | 0.0036 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527-1 | ||
| Elongation at Break | 0.85 % | 0.85 % | ISO 527-1 | ||
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527-1 | ||
| Flexural Strength | 185 MPa | 26800 psi | ISO 178 | ||
| Flexural Modulus | 13.0 GPa | 1890 ksi | ISO 178 | ||
| Compressive Strength | 270 MPa | 39200 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.10 J/cm2 | 5.23 ft-lb/in2 | ISO 179-1 | ||
| Charpy Impact, Notched | 0.350 J/cm2 | 1.67 ft-lb/in2 | ISO 179-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.17e+13 ohm-cm | 3.17e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 2.41e+13 ohm | 2.41e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 22.0 μm/m-°C | 12.2 μin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 44.0 μm/m-°C | 24.4 μin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 188 °C | >= 370 °F | ISO 75 Af | ||
| Flammability, UL94 | V-1 @Thickness 1.50 mm | V-1 @Thickness 0.0591 in | |||
| V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | ||||
| Shrinkage | 0.050 % | 0.050 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Colors | Black, Green | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||