- 密度 [g/cm3]: 2.06
- 吸水率 [%]: 0.04
- 彎曲模量 [MPa]: 26.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 1.00 g/cc | 0.0361 lb/in3 | ISO 60 | ||
| Density | 2.06 g/cc | 0.0744 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.040 % | 0.040 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 89.0 MPa | 12900 psi | ISO 527-1 | ||
| Elongation at Break | 0.35 % | 0.35 % | ISO 527-1 | ||
| Tensile Modulus | 29.0 GPa | 4210 ksi | ISO 527-1 | ||
| Flexural Strength | 163 MPa | 23600 psi | ISO 178 | ||
| Flexural Modulus | 26.0 GPa | 3770 ksi | ISO 178 | ||
| Compressive Strength | 269 MPa | 39000 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.960 J/cm2 | 4.57 ft-lb/in2 | ISO 179-1 | ||
| Charpy Impact, Notched | 0.260 J/cm2 | 1.24 ft-lb/in2 | ISO 179-1 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 14.0 μm/m-°C | 7.78 μin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 30.0 μm/m-°C | 16.7 μin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 222 °C | >= 432 °F | ISO 75 Af | ||
| Shrinkage | 0.010 % | 0.010 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||