- 密度 [g/cm3]: 1.63
- 彎曲模量 [MPa]: 10.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.750 - 0.900 g/cc | 0.0271 - 0.0325 lb/in3 | Powder Density; ISO 60 | ||
| Density | 1.63 g/cc | 0.0589 lb/in3 | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0050 - 0.0060 cm/cm | 0.0050 - 0.0060 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 30.0 - 50.0 MPa | 4350 - 7250 psi | ISO 527 | ||
| Elongation at Break | 0.20 - 0.30 % | 0.20 - 0.30 % | Tensile; ISO 527 | ||
| 0.60 - 0.70 % | 0.60 - 0.70 % | Flexure; ISO 178 | |||
| Tensile Modulus | 13.0 - 15.0 GPa | 1890 - 2180 ksi | ISO 527 | ||
| Flexural Strength | 65.0 - 85.0 MPa | 9430 - 12300 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 10.0 - 12.0 GPa | 1450 - 1740 ksi | ISO 178 | ||
| Compressive Strength | 110 - 130 MPa | 16000 - 18900 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.250 - 0.350 J/cm2 | 1.19 - 1.67 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.150 - 0.250 J/cm2 | 0.714 - 1.19 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 - 30.0 μm/m-°C @Temperature 20.0 °C | 11.1 - 16.7 μin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 20.0 - 30.0 μm/m-°C @Temperature 20.0 °C | 11.1 - 16.7 μin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 150 - 170 °C | 302 - 338 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 130 - 150 °C | 266 - 302 °F | ISO 75 C | ||
| Flammability, UL94 | V-1 @Thickness 1.60 mm | V-1 @Thickness 0.0630 in | |||
| V-0 @Thickness 4.00 mm | V-0 @Thickness 0.157 in | ||||
| Shrinkage | 0.050 - 0.15 % | 0.050 - 0.15 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| ISO type | PF 2 C4 | ||||
| Main Filler | Graphite | ||||
| Molding Method | Compression, transfer, injection | ||||