- 密度 [g/cm3]: 1.84
- 吸水率 [%]: 0.06
- 彎曲模量 [MPa]: 18.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.590 g/cc | 0.0213 lb/in3 | ISO 60 | ||
| Density | 1.84 g/cc | 0.0665 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.060 % | 0.060 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0014 cm/cm | 0.0014 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 101 MPa | 14600 psi | ISO 527-1 | ||
| Elongation at Break | 0.68 % | 0.68 % | ISO 527-1 | ||
| Tensile Modulus | 19.0 GPa | 2760 ksi | ISO 527-1 | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO 178 | ||
| Flexural Modulus | 18.0 GPa | 2610 ksi | ISO 178 | ||
| Compressive Strength | 293 MPa | 42500 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.39 J/cm2 | 6.61 ft-lb/in2 | ISO 179-1 | ||
| Charpy Impact, Notched | 0.330 J/cm2 | 1.57 ft-lb/in2 | ISO 179-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 4.15e+13 ohm-cm | 4.15e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 2.69e+13 ohm | 2.69e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 18.0 kV/mm | 457 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 14.0 μm/m-°C | 7.78 μin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 50.0 μm/m-°C | 27.8 μin/in-°F | TMA | ||
| Thermal Conductivity | 0.450 W/m-K | 3.12 BTU-in/hr-ft2-°F | ASTM E1461 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 223 °C | >= 433 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 171 °C | 340 °F | ISO 75 Cf | ||
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |||
| Shrinkage | 0.040 % | 0.040 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||