- 密度 [g/cm3]: 1.7
- 彎曲模量 [MPa]: 9.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.700 - 0.850 g/cc | 0.0253 - 0.0307 lb/in3 | Powder Density; ISO 60 | ||
| Density | 1.70 g/cc | 0.0614 lb/in3 | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0030 - 0.0040 cm/cm | 0.0030 - 0.0040 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 50.0 - 60.0 MPa | 7250 - 8700 psi | ISO 527 | ||
| Elongation at Break | 0.60 - 0.70 % | 0.60 - 0.70 % | Tensile; ISO 527 | ||
| 1.3 - 1.4 % | 1.3 - 1.4 % | Flexure; ISO 178 | |||
| Tensile Modulus | 9.50 - 11.5 GPa | 1380 - 1670 ksi | ISO 527 | ||
| Flexural Strength | 130 - 150 MPa | 18900 - 21800 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 9.00 - 11.0 GPa | 1310 - 1600 ksi | ISO 178 | ||
| Compressive Strength | 220 - 240 MPa | 31900 - 34800 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.750 - 0.900 J/cm2 | 3.57 - 4.28 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.250 - 0.400 J/cm2 | 1.19 - 1.90 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Insulation Resistance | 1.00e+13 - 1.00e+14 ohm | 1.00e+13 - 1.00e+14 ohm | Dry; IEC 167 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 - 30.0 μm/m-°C @Temperature 20.0 °C | 11.1 - 16.7 μin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 40.0 - 50.0 μm/m-°C @Temperature 20.0 °C | 22.2 - 27.8 μin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 150 - 170 °C | 302 - 338 °F | ISO 75 C | ||
| Shrinkage | 0.15 - 0.30 % | 0.15 - 0.30 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| ISO type | PF 2 C3 | ||||
| Main Filler | Glass Fiber | ||||
| Molding Method | Compression, transfer, injection | ||||