- 密度 [g/cm3]: 1.67
- 彎曲模量 [MPa]: 15.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.750 g/cc | 0.0271 lb/in3 | Powder Density; ISO 60 | ||
| Density | 1.67 g/cc | 0.0603 lb/in3 | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0022 cm/cm | 0.0022 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | ISO 527 | ||
| Elongation at Break | 0.70 % | 0.70 % | Tensile; ISO 527 | ||
| 1.0 % | 1.0 % | Flexure; ISO 178 | |||
| Tensile Modulus | 17.0 GPa | 2470 ksi | ISO 527 | ||
| Flexural Strength | 130 MPa | 18900 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 15.0 GPa | 2180 ksi | ISO 178 | ||
| Compressive Strength | 170 MPa | 24700 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.700 J/cm2 | 3.33 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.300 J/cm2 | 1.43 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C @Temperature 20.0 °C | 11.1 μin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 35.0 μm/m-°C @Temperature 20.0 °C | 19.4 μin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 Af | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 4.00 mm | V-0 @Thickness 0.157 in | ||||
| Shrinkage | 0.010 % | 0.010 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| ISO type | PF 2 C1 | ||||
| Main Filler | Glass Fiber & Graphite | ||||
| Molding Method | Compression, transfer, injection | ||||