- 密度 [g/cm3]: 1.6
- 彎曲模量 [MPa]: 12.5
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 g/cc | 0.0217 lb/in3 | Powder Density; ISO 60 | ||
| Density | 1.60 g/cc | 0.0578 lb/in3 | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527 | ||
| Elongation at Break | 0.90 % | 0.90 % | Tensile; ISO 527 | ||
| 1.6 % | 1.6 % | Flexure; ISO 178 | |||
| Tensile Modulus | 14.0 GPa | 2030 ksi | ISO 527 | ||
| Flexural Strength | 200 MPa | 29000 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 12.5 GPa | 1810 ksi | ISO 178 | ||
| Compressive Strength | 260 MPa | 37700 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.35 J/cm2 | 6.42 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.380 J/cm2 | 1.81 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | DIN 53482 | ||
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 93 | ||
| Insulation Resistance | 5.00e+10 ohm | 5.00e+10 ohm | Wet; 24 hours in water; IEC 167 | ||
| 1.00e+11 ohm | 1.00e+11 ohm | Dry; IEC 167 | |||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243 | ||
| Comparative Tracking Index | 125 V | 125 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 25.0 μm/m-°C @Temperature 20.0 °C | 13.9 μin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 35.0 μm/m-°C @Temperature 20.0 °C | 19.4 μin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 Af | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 4.00 mm | V-0 @Thickness 0.157 in | ||||
| Shrinkage | 0.060 % | 0.060 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black, Green | ||||
| ISO type | PF 2 C1 | ||||
| Main Filler | Glass Fiber | ||||
| Molding Method | Compression, transfer, injection | ||||