- 密度 [g/cm3]: 1.7
- 彎曲模量 [MPa]: 7.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.750 g/cc | 0.0217 - 0.0271 lb/in3 | Powder Density; ISO 60 | ||
| Density | 1.70 g/cc | 0.0614 lb/in3 | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0015 - 0.0025 cm/cm | 0.0015 - 0.0025 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 65.0 - 75.0 MPa | 9430 - 10900 psi | ISO 527 | ||
| Elongation at Break | 1.05 - 1.15 % | 1.05 - 1.15 % | Tensile; ISO 527 | ||
| 1.6 - 1.8 % | 1.6 - 1.8 % | Flexure; ISO 178 | |||
| Tensile Modulus | 9.50 - 11.5 GPa | 1380 - 1670 ksi | ISO 527 | ||
| Flexural Strength | 140 - 160 MPa | 20300 - 23200 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 7.50 - 9.00 GPa | 1090 - 1310 ksi | ISO 178 | ||
| Compressive Strength | 190 - 220 MPa | 27600 - 31900 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.30 - 1.50 J/cm2 | 6.19 - 7.14 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.450 - 0.550 J/cm2 | 2.14 - 2.62 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Insulation Resistance | 1.00e+11 - 1.00e+13 ohm | 1.00e+11 - 1.00e+13 ohm | Dry; IEC 167 | ||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 243 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 20.0 - 30.0 μm/m-°C @Temperature 20.0 °C | 11.1 - 16.7 μin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 30.0 - 40.0 μm/m-°C @Temperature 20.0 °C | 16.7 - 22.2 μin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 170 - 190 °C | 338 - 374 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 150 - 170 °C | 302 - 338 °F | ISO 75 C | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| V-0 @Thickness 4.00 mm | V-0 @Thickness 0.157 in | ||||
| Shrinkage | 0.10 - 0.20 % | 0.10 - 0.20 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| ISO type | PF 2 C3 | ||||
| Main Filler | Glass Fiber & Mineral | ||||
| Molding Method | Compression, transfer, injection | ||||