- 密度 [g/cm3]: 2.08
- 彎曲模量 [MPa]: 25.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 1.05 g/cc | 0.0379 lb/in3 | Powder Density; ISO 60 | ||
| Density | 2.08 g/cc | 0.0751 lb/in3 | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 | ||
| Elongation at Break | 0.40 % | 0.40 % | Tensile; ISO 527 | ||
| 0.75 % | 0.75 % | Flexure; ISO 178 | |||
| Tensile Modulus | 28.0 GPa | 4060 ksi | ISO 527 | ||
| Flexural Strength | 170 MPa | 24700 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 25.0 GPa | 3630 ksi | ISO 178 | ||
| Compressive Strength | 300 MPa | 43500 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.800 J/cm2 | 3.81 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.250 J/cm2 | 1.19 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Insulation Resistance | 1.00e+13 - 1.00e+14 ohm | 1.00e+13 - 1.00e+14 ohm | Dry; IEC 167 | ||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243 | ||
| Comparative Tracking Index | 200 V | 200 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 14.0 μm/m-°C @Temperature 20.0 °C | 7.78 μin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 20.0 μm/m-°C @Temperature 20.0 °C | 11.1 μin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 Af | ||
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | |||
| V-0 @Thickness 4.00 mm | V-0 @Thickness 0.157 in | ||||
| Shrinkage | 0.010 % | 0.010 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Dark Green | ||||
| ISO type | PF 2 C3 | ||||
| Main Filler | Glass Fiber & Mineral | ||||
| Molding Method | Compression, transfer, injection | ||||