- 密度 [g/cm3]: 1.7
- 彎曲模量 [MPa]: 6.00
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.650 - 0.800 g/cc | 0.0235 - 0.0289 lb/in3 | Powder Density; ISO 60 | ||
| Density | 1.70 g/cc | 0.0614 lb/in3 | Relative Density; ISO 1183 | ||
| Linear Mold Shrinkage | 0.0040 - 0.0050 cm/cm | 0.0040 - 0.0050 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 40.0 - 50.0 MPa | 5800 - 7250 psi | ISO 527 | ||
| Elongation at Break | 0.70 - 0.80 % | 0.70 - 0.80 % | Tensile; ISO 527 | ||
| 1.45 - 1.55 % | 1.45 - 1.55 % | Flexure; ISO 178 | |||
| Tensile Modulus | 12.5 - 14.0 GPa | 1810 - 2030 ksi | ISO 527 | ||
| Flexural Strength | 90.0 - 110 MPa | 13100 - 16000 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 6.00 - 8.00 GPa | 870 - 1160 ksi | ISO 178 | ||
| Compressive Strength | 200 - 230 MPa | 29000 - 33400 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.800 - 1.00 J/cm2 | 3.81 - 4.76 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.200 - 0.300 J/cm2 | 0.952 - 1.43 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | DIN 53482 | ||
| Insulation Resistance | 5.00e+10 ohm | 5.00e+10 ohm | Wet; 24 hours in water; IEC 167 | ||
| 1.00e+11 ohm | 1.00e+11 ohm | Dry; IEC 167 | |||
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 243 | ||
| Comparative Tracking Index | 175 V | 175 V | IEC 112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 30.0 - 40.0 μm/m-°C @Temperature 20.0 °C | 16.7 - 22.2 μin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 40.0 - 50.0 μm/m-°C @Temperature 20.0 °C | 22.2 - 27.8 μin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 160 - 180 °C | 320 - 356 °F | ISO 75 Af | ||
| Deflection Temperature at 8.0 MPa | 130 - 150 °C | 266 - 302 °F | ISO 75 C | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| V-0 @Thickness 4.00 mm | V-0 @Thickness 0.157 in | ||||
| Shrinkage | 0.10 - 0.20 % | 0.10 - 0.20 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| ISO type | PF 2 C3 | ||||
| Main Filler | Mineral & Organic | ||||
| Molding Method | Compression, transfer, injection | ||||