- 密度 [g/cm3]: 2.08
- 吸水率 [%]: 0.03
- 彎曲模量 [MPa]: 25.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 1.04 g/cc | 0.0376 lb/in3 | ISO 60 | ||
| Density | 2.08 g/cc | 0.0751 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.030 % | 0.030 % | ISO 62 | ||
| Linear Mold Shrinkage | 0.0015 cm/cm | 0.0015 in/in | ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1 | ||
| Elongation at Break | 0.45 % | 0.45 % | ISO 527-1 | ||
| Tensile Modulus | 30.0 GPa | 4350 ksi | ISO 527-1 | ||
| Flexural Strength | 190 MPa | 27600 psi | ISO 178 | ||
| Flexural Modulus | 25.0 GPa | 3630 ksi | ISO 178 | ||
| Compressive Strength | 360 MPa | 52200 psi | ISO 604 | ||
| Charpy Impact Unnotched | 0.870 J/cm2 | 4.14 ft-lb/in2 | ISO 179-1 | ||
| Charpy Impact, Notched | 0.270 J/cm2 | 1.28 ft-lb/in2 | ISO 179-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.74e+15 ohm-cm | 1.74e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.95e+13 ohm | 1.95e+13 ohm | IEC 60093 | ||
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | IEC 60243-1 | ||
| Comparative Tracking Index | 325 V | 325 V | IEC 60250 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 12.0 μm/m-°C | 6.67 μin/in-°F | TMA | ||
| CTE, linear, Transverse to Flow | 22.0 μm/m-°C | 12.2 μin/in-°F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | >= 223 °C | >= 433 °F | ISO 75 Af | ||
| Flammability, UL94 | V-0 @Thickness 3.00 mm | V-0 @Thickness 0.118 in | |||
| V-0 @Thickness 1.50 mm | V-0 @Thickness 0.0591 in | ||||
| Shrinkage | 0.020 % | 0.020 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Dark Green | ||||
| Molding Method | Compression | ||||
| Injection | |||||
| Transfer | |||||