- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 0.05
- 彎曲模量 [MPa]: 17.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.600 - 0.700 g/cc | 0.0217 - 0.0253 lb/in3 | Powder Density; ISO 60 | ||
| Density | 1.35 g/cc | 0.0488 lb/in3 | Relative Density; ISO 1183 | ||
| Water Absorption | 0.050 - 0.10 % | 0.050 - 0.10 % | |||
| Linear Mold Shrinkage | 0.00 - 0.0020 cm/cm | 0.00 - 0.0020 in/in | Injection Molding; ISO 2577 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 - 130 MPa | 14500 - 18900 psi | ISO 527 | ||
| Elongation at Break | 0.40 - 0.70 % | 0.40 - 0.70 % | Tensile; ISO 527 | ||
| 1.2 - 1.5 % | 1.2 - 1.5 % | Flexure; ISO 178 | |||
| Tensile Modulus | 20.0 - 23.0 GPa | 2900 - 3340 ksi | ISO 527 | ||
| Flexural Strength | 250 - 300 MPa | 36300 - 43500 psi | At Rupture; ISO 178 | ||
| Flexural Modulus | 17.0 - 24.0 GPa | 2470 - 3480 ksi | ISO 178 | ||
| Compressive Strength | 270 - 330 MPa | 39200 - 47900 psi | ISO 604 | ||
| Charpy Impact Unnotched | 1.10 - 1.70 J/cm2 | 5.24 - 8.09 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 0.200 - 0.300 J/cm2 | 0.952 - 1.43 ft-lb/in2 | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 3.817e+7 ohm-cm | 3.817e+7 ohm-cm | ASTM D257 | ||
| Surface Resistance | 3.669e+6 ohm | 3.669e+6 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 1.00 - 5.00 μm/m-°C @Temperature 20.0 °C | 0.556 - 2.78 μin/in-°F @Temperature 68.0 °F | TMA | ||
| CTE, linear, Transverse to Flow | 25.0 - 40.0 μm/m-°C @Temperature 20.0 °C | 13.9 - 22.2 μin/in-°F @Temperature 68.0 °F | TMA | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 230 - 250 °C | 446 - 482 °F | ISO 75 A | ||
| Shrinkage | 0.00 - 0.10 % | 0.00 - 0.10 % | Post Shrinkage; ISO 2577 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Main Filler | Carbon Fiber | ||||
| Molding Method | Compression, transfer, injection | ||||